ExxonMobil LD 312.82 High Impact Film Resin

Category	Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer	Exxon Chemical
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LD 312.82 High Impact Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LD 312 Series films have superior impact strength, good heat sealability, and good low temperature properties. Applications include frozen and other food packaging.Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.925 g/cc	0.0334 lb/in³	ExxonMobil Method
Vinyl Acetate Content	4.6 %	4.6 %	ExxonMobil Method
Thickness	38.1 microns	1.50 mil
Melt Flow	1.0 g/10 min	1.0 g/10 min	ExxonMobil Method
Antiblock Level	4000 ppm	4000 ppm
Slip Level	800 ppm	800 ppm

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	8.27 MPa	1200 psi	at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD	7.93 MPa	1150 psi	at 2% offset; ASTM D882
Film Elongation at Break, MD	180 %	180 %	ASTM D882
Film Elongation at Break, TD	580 %	580 %	ASTM D882
Film Elongation at Yield, MD	6.9 %	6.9 %	ASTM D882
Film Elongation at Yield, TD	5.6 %	5.6 %	ASTM D882
Elmendorf Tear Strength MD	200 g	200 g	ASTM D1922
Elmendorf Tear Strength TD	90 g	90 g	ASTM D1922
Elmendorf Tear Strength, MD	5.248 g/micron	133.3 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	2.36 g/micron	60.0 g/mil	ASTM D1922
Dart Drop	4.984 g/micron	126.6 g/mil	ASTM D1709
Dart Drop Test	190 g	0.419 lb	ASTM D1709
Film Tensile Strength at Break, MD	25.9 MPa	3760 psi	ASTM D882
Film Tensile Strength at Break, TD	24.7 MPa	3580 psi	ASTM D882
1% Secant Modulus, MD	146 MPa	21200 psi	ASTM D882
1% Secant Modulus, TD	168 MPa	24400 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	104 °C	220 °F	Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature	91.0 °C	196 °F	ExxonMobil Method
Vicat Softening Point	88.9 °C	192 °F	ASTM D1525

Optical Properties	Metric	English	Comments
Haze	6.4 %	6.4 %	ASTM D1003
Gloss	71 %	71 %	45°; ASTM D2457

Descriptive Properties	Value	Comments
Features	Thermal Stabilizer