ExxonMobil LD 103.MP Industrial Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LD 103.MP Industrial Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LD 103 resins are homopolymer industrial film resins are used in box and drum liners, industrial packaging, medium duty shrink wrap, construction and agriculture film, and rubber bale wrap.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.919 g/cc
0.0332 lb/in³
ExxonMobil Method
Thickness 38.1 microns
1.50 mil
Melt Flow 1.05 g/10 min
1.05 g/10 min
ExxonMobil Method
Antiblock Level 5000 ppm
5000 ppm
Slip Level 500 ppm
500 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.5 MPa
1530 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 10.4 MPa
1510 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 120 %
120 %
ASTM D882
Film Elongation at Break, TD 540 %
540 %
ASTM D882
Film Elongation at Yield, MD 6.3 %
6.3 %
ASTM D882
Film Elongation at Yield, TD 5.1 %
5.1 %
ASTM D882
Elmendorf Tear Strength MD 340 g
340 g
ASTM D1922
Elmendorf Tear Strength TD 80 g
80 g
ASTM D1922
Elmendorf Tear Strength, MD 8.921 g/micron
226.6 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 2.100 g/micron
53.33 g/mil
ASTM D1922
Dart Drop 3.41 g/micron
86.6 g/mil
ASTM D1709
Dart Drop Test 130 g
0.287 lb
ASTM D1709
Film Tensile Strength at Break, MD 25.7 MPa
3730 psi
ASTM D882
Film Tensile Strength at Break, TD 20.7 MPa
3000 psi
ASTM D882
1% Secant Modulus, MD 199 MPa
28900 psi
ASTM D882
1% Secant Modulus, TD 256 MPa
37200 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 107 °C
225 °F
Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature 95.0 °C
203 °F
ExxonMobil Method
Vicat Softening Point 91.7 °C
197 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 12.7 %
12.7 %
ASTM D1003
Gloss 49 %
49 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer