ExxonMobil LD 071.LR Blown Film Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer	Exxon Chemical
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LD 071.LR Blown Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LD 071 Series case wrap film resins combine good processability with excellent strength and good film optics for bundling applications requiring proper shrink performance, toughness, burn-through resistance and clarity. Availability: Latin America, North America and South America Additive: Antiblock: 2000 ppmSlip: NoThermal Stabilizer: NoApplications:Blend PartnerCo-Extrusion FilmsCollation ShrinkConstruction FilmForm Fill and Seal PackagingFreezer FilmLamination FilmMedium Duty Shrink FilmPallet Shrink Film Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.924 g/cc	0.0334 lb/in³	ExxonMobil Method
Thickness	50.8 microns	2.00 mil
Antiblock Level	2000 ppm	2000 ppm

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	11.0 MPa	1600 psi	ASTM D882
Film Tensile Strength at Yield, TD	11.8 MPa	1710 psi	ASTM D882
Film Elongation at Break, MD	130 %	130 %	ASTM D882
Film Elongation at Break, TD	540 %	540 %	ASTM D882
Puncture Energy	0.859 J	0.633 ft-lb	ExxonMobil Method
Elmendorf Tear Strength MD	510 g	510 g	ASTM D1922
Elmendorf Tear Strength TD	140 g	140 g	ASTM D1922
Dart Drop Test	170 g	0.375 lb	ASTM D1709
Film Tensile Strength at Break, MD	25.5 MPa	3700 psi	ASTM D882
Film Tensile Strength at Break, TD	22.1 MPa	3200 psi	ASTM D882
1% Secant Modulus, MD	234 MPa	34000 psi	ASTM D882
1% Secant Modulus, TD	290 MPa	42000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	112 °C	234 °F	Peak Melting Temperature; ExxonMobil Method

Optical Properties	Metric	English	Comments
Haze	9.6 %	9.6 %	ASTM D1003
Gloss	57 %	57 %	45°; ASTM D2457