Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Blow Molding Grade |
Manufacturer | Exxon Chemical |
Trade Name | Exceed™ |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | ExxonMobil Exceed™ 4518PA Premium Cast Film Resin.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.918 g/cc | 0.0332 lb/in³ | ExxonMobil Method |
Melt Flow | 4.5 g/10 min | 4.5 g/10 min | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Yield, MD | 8.34 MPa | 1210 psi | at 2% offset; ASTM D882 |
Film Tensile Strength at Yield, TD | 7.31 MPa | 1060 psi | at 2% offset; ASTM D882 |
Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 |
Film Elongation at Break, TD | 730 % | 730 % | ASTM D882 |
Puncture Energy | 4.41 J | 3.25 ft-lb | Exxon Mobil Method |
Elmendorf Tear Strength, MD | 7.382 g/micron | 187.5 g/mil | ASTM D1922 |
Elmendorf Tear Strength, TD | 22.6 g/micron | 575 g/mil | ASTM D1922 |
Dart Drop | 6.89 g/micron | 175 g/mil | ASTM D1709A |
Film Tensile Strength at Break, MD | 66.9 MPa | 9700 psi | ASTM D882 |
Film Tensile Strength at Break, TD | 48.1 MPa | 6970 psi | ASTM D882 |
1% Secant Modulus, MD | 101 MPa | 14700 psi | ASTM D882 |
1% Secant Modulus, TD | 124 MPa | 18000 psi | ASTM D882 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Melting Point | 114 °C | 237 °F | Peak Melting Temperature; ExxonMobil Method |
Optical Properties | Metric | English | Comments |
---|---|---|---|
Haze | 2.2 % | 2.2 % | ASTM D1003 |
Gloss | 87 % | 87 % | 45°; ASTM D2457 |
Descriptive Properties | Value | Comments |
---|---|---|
Features | Thermal Stabilizer |