ExxonMobil Exceed™ 377D60 LDPE/Hexene Tough Premium Film Resin, 0.8 mil Film  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Exceed™ 377D60 LDPE/Hexene Tough Premium Film Resin, 0.8 mil Film  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A hexene copolymer produced using Exxon Chemical's EXXPOL® technology. Films made from EXCEED 377D60 resin exhibit excellent impact strength and balanced tensile and tear.Applications: Shipping sacks; Heavy duty bags; Trash bag; Liners; General packaging. Data for film properties below based on 0.8 mil film.
Physical Properties Metric English Comments
Density 0.922 g/cc
0.0333 lb/in³
Exxon Method
Thickness 20.3 microns
0.800 mil
Melt Flow 1.0 g/10 min
1.0 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.8 MPa
1570 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.5 MPa
1670 psi
ASTM D882
Film Elongation at Break, MD 480 %
480 %
ASTM D882
Film Elongation at Break, TD 600 %
600 %
ASTM D882
Secant Modulus, MD 0.237 GPa
34.4 ksi
ASTM D882
Secant Modulus, TD 0.246 GPa
35.7 ksi
ASTM D882
Coefficient of Friction 0.69
0.69
ASTM D1894
Elmendorf Tear Strength MD 190 g
190 g
ASTM D1922
Elmendorf Tear Strength TD 390 g
390 g
ASTM D1922
Elmendorf Tear Strength, MD 9.37 g/micron
238 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 19.2 g/micron
488 g/mil
ASTM D1922
Dart Drop 22.2 g/micron
563 g/mil
F50; ASTM D1709
Dart Drop Test 450 g
0.992 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 60.0 MPa
8700 psi
ASTM D882
Film Tensile Strength at Break, TD 56.0 MPa
8120 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 120 °C
248 °F
Exxon Method