ExxonMobil Exceed™ 1018KB Metallocene Polyethylene Resin (European Grade)

Category	Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer	Exxon Chemical
Trade Name	Exceed™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Exceed™ 1018KB Metallocene Polyethylene Resin (European Grade).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: Exceed 1018KB is a metallocene ethylene-hexene copolymers. Films are made of Exceed 1018KB resin have outstanding tensile, impact strength and puncture. These superior strength properties, along with excellent drawability, allow downgauging in bag application.Availability: Africa & Middle East and EuropeAdditive:Antiblock: 2500 ppmSlip:800 ppm Processing Aid: Yes Thermal Stabilizer: Yes Applications:Agricultural FilmBag in a BoxBarrier Food Packaging Blown FilmBread Bags Food packagingForm Fill and Seal PackagingFreezer FilmGeneral PackagingHeavy Duty BagsLamination FilmMultilayer Packaging FilmOverwrap FilmPackaging FilmsPremium Trash BagsStand Up PouchesTrash BagsTrash Can Liners Information provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.918 g/cc	0.0332 lb/in³	ExxonMobil method
Melt Flow	1.0 g/10 min @Load 2.16 kg, Temperature 190 °C	1.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Antiblock Level	2500 ppm	2500 ppm
Slip Level	800 ppm	800 ppm

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	9.65 MPa	1400 psi	ASTM D882
Film Tensile Strength at Yield, TD	9.65 MPa	1400 psi	ASTM D882
Film Elongation at Break, MD	500 %	500 %	ASTM D882
Film Elongation at Break, TD	600 %	600 %	ASTM D882
Elmendorf Tear Strength MD	250 g	250 g	ASTM D1922
Elmendorf Tear Strength TD	470 g	470 g	ASTM D1922
Dart Drop Test	590 g	1.30 lb	ASTM D1709
Film Tensile Strength at Break, MD	54.5 MPa	7900 psi	ASTM D882
Film Tensile Strength at Break, TD	42.7 MPa	6200 psi	ASTM D882
1% Secant Modulus, MD	186 MPa	27000 psi	ASTM D882
1% Secant Modulus, TD	193 MPa	28000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 247 °C	<= 477 °F	Peak Melting Point; ExxonMobil method

Optical Properties	Metric	English	Comments
Haze	18 %	18 %	ASTM D1003
Gloss	39 %	39 %	45°; ASTM D2457