ExxonMobil Escorene® LD 728.61 Molding, extrusion and compounding resin

Category	Polymer , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Extrusion/Coating Grade
Manufacturer	Exxon Chemical
Trade Name	Escorene®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene® LD 728.61 Molding, extrusion and compounding resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Escorene Ultra LD 728.61 is a high vinyl acetate copolymer with low melting temperature and excellent strength properties and toughness.Availability: Latin America, North America and South America Additive: Thermal Stabilizer: Yes Applications:FoamsInjection MoldingProfile ExtrusionShoe SolesInformation provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.935 g/cc	0.0338 lb/in³	ExxonMobil Method
Vinyl Acetate Content	18.2 %	18.2 %	ExxonMobil Method
Melt Flow	2.00 g/10 min @Load 2.16 kg, Temperature 190 °C	2.00 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	76	76	15s; ASTM D2240
Hardness, Shore D	36	36	15s; ASTM D2240
Tensile Strength at Break	11.7 MPa	1700 psi	ASTM D638
Tensile Strength, Yield	5.24 MPa	760 psi	ASTM D638
Elongation at Break	>= 800 %	>= 800 %	ASTM D638
Elongation at Yield	260 %	260 %	ASTM D638
Flexural Modulus	0.0607 GPa	8.80 ksi	1% secant; ASTM D790
Impact Test	17.6 J @Temperature 23.0 °C	13.0 ft-lb @Temperature 73.4 °F	Instrument Impact, Total Energy; ASTM D3763
	35.3 J @Temperature -40.0 °C	26.0 ft-lb @Temperature -40.0 °F	Instrumented Impact, Total Energy; ASTM D3763

Thermal Properties	Metric	English	Comments
Melting Point	87.2 °C	189 °F	Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point	63.9 °C	147 °F	ASTM D1525