ExxonMobil Escorene® LD 319.92 Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Escorene® LD 319.92 Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Escorene Ultra LD 319.92 is a 9.0 wt% vinyl acetate copolymer film resin, that exhibits superior impact strength and heat sealability.Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ExxonMobil Method |
| Vinyl Acetate Content | 9.0 % | 9.0 % | ExxonMobil Method |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 6.89 MPa | 1000 psi | at 2% offset; ASTM D882 |
| Film Tensile Strength at Yield, TD | 6.27 MPa | 910 psi | at 2% offset; ASTM D882 |
| Film Elongation at Break, MD | 330 % | 330 % | ASTM D882 |
| Film Elongation at Break, TD | 660 % | 660 % | ASTM D882 |
| Film Elongation at Yield, MD | 7.9 % | 7.9 % | ASTM D882 |
| Film Elongation at Yield, TD | 6.4 % | 6.4 % | ASTM D882 |
| Elmendorf Tear Strength, MD | 3.15 g/micron | 80.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 2.625 g/micron | 66.67 g/mil | ASTM D1922 |
| Dart Drop | 6.5618 g/micron | 166.67 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 30.5 MPa | 4430 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 27.4 MPa | 3980 psi | ASTM D882 |
| 1% Secant Modulus, MD | 106 MPa | 15400 psi | ASTM D882 |
| 1% Secant Modulus, TD | 116 MPa | 16800 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 98.9 °C | 210 °F | Peak Melting Temperature; ExxonMobil Method |
| Crystallization Temperature | 85.0 °C | 185 °F | ExxonMobil Method |
| Vicat Softening Point | 80.6 °C | 177 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.5 % | 1.5 % | ASTM D1003 |
| Gloss | 88 % | 88 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |
Users viewing this material also viewed the following:
- Pasargad Polymer Peyvand Pasalen 3P-H3230B1 Polypropylene, 30% Mineral Filled Reinforced
- Polymer Resources PC-HM-FR1-[color]-1 Polycarbonate, 10% Glass Reinforced, Flame Retardant with Mold Release
- Saint-Gobain Spectrosil® 2100 Optical Fused Quartz
- SABIC Innovative Plastics LNP THERMOCOMP MF006SXP PP
- Tisan TISMOSET®
- Dow INTEGRAL™ 900 Deep Draw Multilayer Adhesive Film
- Arlon 55636R025 0.025" Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Arlon 55276R030 0.030" (0.762 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- SABIC Innovative Plastics Lexan® HPH4504H PPC
- HP Alloys Nitronic® 50 Austenitic Stainless, Level 5 Cold Worked
Copyright © lookpolymers.com All Rights Reserved