ExxonMobil Escorene® LD-108 LDPE Packaging Film Resin, High Clarity  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LD-108 LDPE Packaging Film Resin, High Clarity  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A homopolymer high clarity film resin with a good balance of toughness, stiffness, and drawdown capability. This resin has good machinability in bag making equipment and can be drawn down to less than 1.0 mil in the blown film process.Applications: Food packaging (sandwich bags, baked goods bags, light duty produce bags, etc.); Textile goods packaging (shirts, sweaters, etc.); Clarity packaging applications requiring a softer film. Data for film properties below based on 1.25 mil film.
Physical Properties Metric English Comments
Density 0.923 g/cc
0.0333 lb/in³
Exxon Method
Thickness 31.8 microns
1.25 mil
Melt Flow 2.0 g/10 min
2.0 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 12.0 MPa
1740 psi
ASTM D882
Film Tensile Strength at Yield, TD 12.0 MPa
1740 psi
ASTM D882
Film Elongation at Break, MD 100 %
100 %
ASTM D882
Film Elongation at Break, TD 500 %
500 %
ASTM D882
Secant Modulus, MD 0.240 GPa
34.8 ksi
ASTM D882
Secant Modulus, TD 0.280 GPa
40.6 ksi
ASTM D882
Elmendorf Tear Strength MD 500 g
500 g
ASTM D1922
Elmendorf Tear Strength TD 100 g
100 g
ASTM D1922
Elmendorf Tear Strength, MD 15.7 g/micron
400 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 3.15 g/micron
80.0 g/mil
ASTM D1922
Dart Drop 1.89 g/micron
48.0 g/mil
F50; ASTM D1709
Dart Drop Test 60.0 g
0.132 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 33.0 MPa
4790 psi
ASTM D882
Film Tensile Strength at Break, TD 17.0 MPa
2470 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 112 °C
234 °F
Exxon Method
Optical Properties Metric English Comments
Haze 6.0 %
6.0 %
ASTM D1003
Gloss 65 %
65 %
45°, ASTM D-2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified