- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyethylene (PE)
- HDPE
- High Density Polyethylene (HDPE), Injection Molded
- ExxonMobil Escorene® HD-6704 HDPE, Injection Grade (discontinued **)
ExxonMobil Escorene® HD-6704 HDPE, Injection Grade (discontinued **)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Escorene® HD-6704 HDPE, Injection Grade
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data Provided by Exxon Chemical Canada.Characteristics: Excellent Toughness, Excellent Stiffness, Excellent ESCRUses: Industrial containers, Industrial lids
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in³ | ASTM D4883 |
| Environmental Stress Crack Resistance | 16 hour | 16 hour | F-50; 10% Igepal Cond. B; ASTM D-1693 |
| Linear Mold Shrinkage | 0.017 cm/cm | 0.017 in/in | Exxon Method |
| Melt Flow | 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Spiral Flow | 33.0 cm | 13.0 in | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 24.8 MPa | 3600 psi | ASTM D638 |
| Elongation at Yield | 17 % | 17 % | ASTM D638 |
| Flexural Modulus | 0.676 GPa | 98.0 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 132 °C | 270 °F | Exxon Method |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Nozzle Temperature | 260 °C | 500 °F | Nozzle (Melt) |
Users viewing this material also viewed the following:
- Polymax® Maxelast® A9845 TPE, ABS/PC Overmold
- Overview of materials for PVC, Extruded
- Mitsubishi Hostaphan® RN, 12 micron Nominal Thickness Universal Polyethylene Terephthalate Film
- Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F)
- Sylvin Technologies 8915-80 Natural PVC Extrusion Compound
- Spartech Noryl® GTX SP-52Z1 Structural Sheet
- Covestro Makrolon® XT5010 Polycarbonate
- CP-Polymer-Technik Wellamid® 6600 HWS Nylon 66, Finely Crystalline, Heat Stabilized, Conditioned
- CP-Polymer-Technik Wellamid® 6600 MR 309 HWCP 30% Mineral Nylon 66, Heat Stabilized, Conditioned
- BASF Ultraform® N2320 0035 POM
Copyright © lookpolymers.com All Rights Reserved