ExxonMobil Enable™ 27-05HH Metallocene Polyethylene Resin (European Grade)

Category	Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer	Exxon Chemical
Trade Name	Enable™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Enable™ 27-05HH Metallocene Polyethylene Resin (European Grade).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: Enable 27-05HH is a metallocene ethylene-hexene copolymers. Enable mPE resins offer an outstanding balance between processing and film properties, including tensile, impact and puncture. Easier processing and excellent properties lead to significant high pressure LDPE replacement in many applications, yet with superior drawdown and enhanced toughness. Availability: Africa & Middle East, Asia Pacific and EuropeAdditive:Antiblock: NoSlip: NoProcessing Aid: YesThermal Stabilizer: YesApplications:Blown FilmCollation ShrinkFood packagingForm Fill and Seal PackagingHeavy Duty BagsLamination FilmMultilayer Packaging FilmShrink FilmStand Up Pouches Information provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.927 g/cc	0.0335 lb/in³	ExxonMobil method
Melt Flow	0.50 g/10 min @Load 2.16 kg, Temperature 190 °C	0.50 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	13.1 MPa	1900 psi	ASTM D882
Film Tensile Strength at Yield, TD	14.5 MPa	2100 psi	ASTM D882
Film Elongation at Break, MD	520 %	520 %	ASTM D882
Film Elongation at Break, TD	770 %	770 %	ASTM D882
Elmendorf Tear Strength MD	50 g	50 g	ASTM D1922
Elmendorf Tear Strength TD	730 g	730 g	ASTM D1922
Dart Drop Test	130 g	0.287 lb	ASTM D1709
Film Tensile Strength at Break, MD	58.6 MPa	8500 psi	ASTM D882
Film Tensile Strength at Break, TD	50.3 MPa	7300 psi	ASTM D882
1% Secant Modulus, MD	296 MPa	43000 psi	ASTM D882
1% Secant Modulus, TD	352 MPa	51000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 246 °C	<= 475 °F	Peak Melting Point; ExxonMobil method

Optical Properties	Metric	English	Comments
Haze	11 %	11 %	ASTM D1003
Gloss	49 %	49 %	45°; ASTM D2457