ExxonMobil Bicor™ 20MB666 OPP Film

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer	Exxon Chemical
Trade Name	Bicor™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Bicor™ 20MB666 OPP Film.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Product Description: Bicor 20MB666 is a biaxially oriented transparent polypropylene film acrylic coated two sides. It provides outstanding performance on all packaging machines and is mainly proposed for use in lamination.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Low sealing thresholdHigh seal strength even under low pressure sealing conditionsGood aroma barrierExcellent packaging machine performanceOutstanding optical propertiesIdeal support for normal ink systemsWater based coatingsFeatures:Acrylic CoatedFlavor & Aroma BarrierIn Lamination Lap SealableApplications: Biscuits/Cookies/CrackersBox OverwrapConfectionery, Chocolate Confectionery, Gum Confectionery, SugarCrisps and Snacks Health and Beauty CareHousehold and Detergents Pet Food Uses:Box Overwrap Flexible PackagingHFFS Flexible Packaging Pre-made Bags – Flexible PackagingVFFS Flexible Packaging Processing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Water Vapor Transmission	1.40 g/m²/day @Temperature 23.0 °C	0.0900 g/100 in²/day @Temperature 73.4 °F	85% RH; ExxonMobil Method
	6.98 g/m²/day @Temperature 38.0 °C	0.450 g/100 in²/day @Temperature 100 °F	90% RH; ExxonMobil Method
Oxygen Transmission Rate	1000 cc/m²/day @Temperature 23.0 °C	64.5 cc/100 in²/day @Temperature 73.4 °F	Wet, 75% RH; ExxonMobil Method
	1010 cc/m²/day @Temperature 23.0 °C	65.0 cc/100 in²/day @Temperature 73.4 °F	0% RH; ExxonMobil Method
Thickness	20.1 microns	0.790 mil	ExxonMobil Method
Coating Weight	17.9 g/m²	11.2 lb/ream	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	175 %	175 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD	60 %	60 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity	2.00 GPa	290 ksi	MD; ExxonMobil Method
	3.80 GPa	551 ksi	TD; ExxonMobil Method
Coefficient of Friction	0.25	0.25	Both Sides; ExxonMobil Method
Seal Strength	560 g/25 mm @Pressure 0.276 MPa, Temperature 130 °C	560 g/in @Pressure 40.0 psi, Temperature 266 °F	Otto Bruger, 0.2 sec; ExxonMobl Method
Film Tensile Strength at Break, MD	160 MPa	23200 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method

Thermal Properties	Metric	English	Comments
Shrinkage, MD	6.0 %	6.0 %	ExxonMobil Method
Shrinkage, TD	5.5 % @Temperature 135 °C	5.5 % @Temperature 275 °F	ExxonMobil Method

Optical Properties	Metric	English	Comments
Haze	1.2 %	1.2 %	ExxonMobil Method
Gloss	85 %	85 %	45°; ExxonMobil Method

Descriptive Properties	Value	Comments
Heat Seal Range	90°F	36.3 psi, 0.2 sec
Yield	38700 in²/lb