ExxonMobil Bicor™ 15MB400 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor™ 15MB400 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Bicor 15MB400 is one side treated, sealable coextruded OPP film. It is designed for use in laminations.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Outstanding optical propertiesGood seal strengthGood dimensional stabilityGood hot slipGood hot tackFeatures:In Lamination Lap SealableApplications:BakeryBiscuits/Cookie/Crackers Confectionery, Chocolate Confectionery, Gum Confectionery, SugarCrisps and SnacksFresh ProduceFrozen FoodHealth and Beauty CareHousehold and DetergentsIce CreamPet FoodUses:HFFS Flexible Packaging Pre-made Bags – Flexible PackagingVFFS Flexible PackagingProcessing Method: Outer Web Adhesive Lamination, Outer Web Extrusion Lamination, Solvent Flexographic Printing and Solvent Rotogravure PrintingInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 1.55 g/m²/day @Temperature 23.0 °C |
0.100 g/100 in²/day @Temperature 73.4 °F |
85% RH; ExxonMobil Method |
| 7.76 g/m²/day @Temperature 38.0 °C |
0.500 g/100 in²/day @Temperature 100 °F |
90% RH; ExxonMobil Method | |
| Thickness | 15.0 microns | 0.590 mil | ExxonMobil Method |
| Coating Weight | 13.4 g/m² | 8.40 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 205 % | 205 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 55 % | 55 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | MD; ExxonMobil Method |
| 3.50 GPa | 508 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.30 | 0.30 | Untreated; ExxonMobil Method |
| Seal Strength | 300 g/25 mm @Pressure 0.138 MPa, Temperature 115 °C |
300 g/in @Pressure 20.0 psi, Temperature 239 °F |
0.8 sec, Untreated; ExxonMobl Method |
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 290 MPa | 42100 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 5.0 % @Temperature 135 °C, Time 432 sec |
5.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 5.0 % @Temperature 135 °C, Time 432 sec |
5.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.7 % | 1.7 % | ExxonMobil Method |
| Gloss | 85 % | 85 % | 45°; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Seal Range | 54°F | 36.3 psi, 0.2 sec |
| Yield | 51500 in2/lb |
Users viewing this material also viewed the following:
- ExxonMobil Santoprene® 281-55MED Thermoplastic Elastomer (discontinued **)
- Ineos ABS Lustran® 750 ABS, Molding Grade
- Techmer ES Elastoblend® PA6 GF25 IM HS L BK 25% Glass Filled
- Samsung Cheil Industries Starex® HG-0760 ABS, Unreinforced
- SABIC Innovative Plastics LNP VERTON RV00ASXP PA 66 (Europe-Africa-Middle East)
- Zotefoams Plastazote® HD60 High Density Polyethylene Foam
- A. Schulman POLYBATCH™ U-4444-E Blowing Agent Concentrate Based In PE
- Dow Corning SYL-OFF® 7676 RELEASE COATING
- ExxonMobil Mobil Glygoyle 150
Copyright © lookpolymers.com All Rights Reserved