- ExxonMobil Bicor® 120 CSR-2 OPP Film
ExxonMobil Bicor® 120 CSR-2 OPP Film
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor® 120 CSR-2 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Bicor CSR-2 is a one-side treated OPP film designed for cold seal release, either unsupported or as the outer web of a lamination.Availability: Latin America, North America and South AmericaKey Features:Excellent cold seal adhesion and ink adhesion on the treated surfaceNon-migratory slip system for consistent COFExcellent release from cold seal adhesivesApplications:BakeryBiscuits/Cookie/Crackers Confectionery, ChocolateDairy ProductsFresh Produce Uses:HFFS Flexible Packaging VFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Outer Web Adhesive Lamination, Outer Web Extrusion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported and Water-based Flexographic PrintingInformation provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 4.30 g/m²/day | 0.277 g/100 in²/day | 38°C, 90% RH; ExxonMobil Method |
| Thickness | 30.5 microns | 1.20 mil | Nominal; ExxonMobil Method |
| Coating Weight | 27.4 g/m² | 17.1 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Coefficient of Friction | 0.20 | 0.20 | slip modified; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 124 MPa | 18000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 4.0 % | 4.0 % | at 275°F; ExxonMobil Method |
| Shrinkage, TD | 4.0 % | 4.0 % | at 275°F; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.0 % | 2.0 % | ExxonMobil Method |
| Gloss | 88 % | 88 % | 45°, Untreated Surface; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Wetting Tension | 0.83 receding COS theta | Treated Surface |
| Yield | 25200 in2/lb |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1301-0793 PPS, linear, with glass fiber
- Menzolit Menzolit® SMC 1600 Unsaturated Polyester UP
- Kraton® G1641 H (SEBS) Linear Triblock Copolymer
- SABIC Innovative Plastics LNP LUBRICOMP UCL36S PPA
- SABIC Innovative Plastics LNP THERMOCOMP DF006HL PC
- Teknor Apex Sinpolene CPP2020 Polypropylene
- A. Schulman POLYTROPE™ TPP 510 Injection Molding Grade Olefinic Thermoplastic Elastomer
- A. Schulman CP814-01 Linear, Low-Density Polyethylene
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.5 PHR Sulfur
Copyright © lookpolymers.com All Rights Reserved