Eurostar Starglas GX061104 PSU
| Category | Polymer , Thermoplastic , Polysulfone (PSU) |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starglas |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starglas GX061104 PSU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starglas GX061104 is a PSU resin (also known as Starglas PSU A ¾)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Water Absorption | 0.0030 % @Temperature 23.0 °C, Time 86400 sec |
0.0030 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 4.00 mm |
0.0060 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 |
| Elongation at Yield | 5.9 % | 5.9 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.50 GPa | 363 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 113 MPa | 16400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.60 GPa | 377 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 151 °C | 304 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 310 - 330 °C | 590 - 626 °F | |
| Zone 2 | 310 - 330 °C | 590 - 626 °F | |
| Zone 3 | 310 - 330 °C | 590 - 626 °F | |
| Melt Temperature | 310 - 330 °C | 590 - 626 °F | |
| Mold Temperature | 150 °C | 302 °F | |
| Drying Temperature | 120 - 150 °C @Time 14400 sec |
248 - 302 °F @Time 4.00 hour |
|
| Moisture Content | 0.050 % | 0.050 % |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible A44565 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Dielectric Polymers NT-490 Polyimide Label Stock (discontinued **)
- GrafTech eGRAF® HITHERM™ HT-2510 Graphite with Polymer Additive
- Lanxess Durethan® BKV 215 W1 902176 Copolyamide, 15% Glass Fiber
- Stir SpA T 75 BZ AF (PVC)
- A. Schulman PP 828S-01 Polypropylene Medium Impact Molding Grade Polypropylene
- ThyssenKrupp 74NiCr2 Saw Steel, Hot-Rolled Strip
- 3M Scotch-Weld™ DP-100NS Epoxy Adhesive
- PolyOne Edgetek® ES-06CF-09GF/000 RED Polyethersulfone - 6% Carbon - 9% Glass Fiber Reinforced - ESD Applications &
Copyright © lookpolymers.com All Rights Reserved