- Entec Hypro™ PPH-GF30 Natural Homopolymer Polypropylene, 30% Glass Reinforced
Entec Hypro™ PPH-GF30 Natural Homopolymer Polypropylene, 30% Glass Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Entec Engineered Resins |
| Trade Name | Hypro™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Entec Hypro™ PPH-GF30 Natural Homopolymer Polypropylene, 30% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Entec
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Melt Flow | 10.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
10.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 93.0 MPa | 13500 psi | ASTM D638 |
| Elongation at Break | 4.00 % | 4.00 % | ASTM D638 |
| Elongation at Yield | 3.00 % | 3.00 % | ASTM D638 |
| Flexural Strength | 116 MPa | 16800 psi | ASTM D790 |
| Flexural Modulus | 5.448 GPa | 790.2 ksi | tangent; ASTM D790 |
| Izod Impact, Notched | 0.960 J/cm @Thickness 3.17 mm |
1.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL6414 PC (Asia Pacific)
- Karina E 818-35/1-Y-SN-ERM Ivory PVC Compound
- Mearthane Durethaneâ„¢ S DS-385A Solid Polyurethane Elastomer
- Special Metals INCOLOY® Alloy 330
- SABIC Innovative Plastics NORYL GTX GTX810 PPE+PS+PA
- UBE 1024FD-1 Nylon 6 Film
- A. Schulman SCHULAMID® 66 MK4015H 40% Glass Fiber/Mineral Reinforced, Heat Stabilized Nylon 66
- A. Schulman POLYTROPE™ TPP 1010HF-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer
- Chem Polymer Chemlon 125-15 MG Nylon 66, 25% Mineral/15% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved