Elektro-Isola Etronit IIQ S AL Phenolic, Paper Reinforcement, Black with foil, Sheets

Category	Polymer , Thermoset , Phenolic
Manufacturer	Elektro-Isola
Trade Name	Etronit
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Elektro-Isola Etronit IIQ S AL Phenolic, Paper Reinforcement, Black with foil, Sheets.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Description: Mechanically a good Etronit type with electrical properties adequate for insulation in low-voltage applications. Material is black throughout. Elegant surface finish combined with good mechanical strength and electrical properties for use in low-voltage applications. Foil on both sides to protect the surface during processing, transport and installation. The foil may subsequently be removed from the finished componentsInformation provided by Elektro-Isola

Physical Properties	Metric	English	Comments
Density	1.35 g/cc	0.0488 lb/in³	24hr/23°C/50% RH; ISO 1183-A; IEC/EN 60893-2 8.1
Water Absorption	2.67 %	2.67 %	24hr/50°C+24hr in water at 23°C,Test Specimen 50x50x3[mm]; ISO 62-1; IEC/EN 60893-2 8.2

Mechanical Properties	Metric	English	Comments
Tensile Strength	140 MPa <br>@Thickness >=1.50 mm	20300 psi <br>@Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6
Modulus of Elasticity	8.00 GPa <br>@Thickness >=1.50 mm	1160 ksi <br>@Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2
Flexural Strength	170 MPa <br>@Thickness >=1.50 mm	24700 psi <br>@Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1
Compressive Strength	320 MPa <br>@Thickness >=5.00 mm	46400 psi <br>@Thickness >=0.197 in	24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3
Shear Strength	35.0 MPa <br>@Thickness >=5.00 mm	5080 psi <br>@Thickness >=0.197 in	24hr/23°C/50% RH; IEC/EN 60893-2 5.5
Izod Impact, Notched (ISO)	3.50 kJ/m² <br>@Thickness >=5.00 mm	1.67 ft-lb/in² <br>@Thickness >=0.197 in	24hr/23°C/50% RH; ISO 180/2A; IEC/EN 60893-2 5.4.3

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Inert	120 °C <br>@Thickness 0.000 mm,<br> Time 7.20e+7 sec	248 °F <br>@Thickness 0.000 in,<br> Time 20000 hour	IEC 60216; IEC/EN 60893-2 7.1

Electrical Properties	Metric	English	Comments
Insulation Resistance	1.00e+8 ohm <br>@Thickness >=3.00 mm	1.00e+8 ohm <br>@Thickness >=0.118 in	24hr/50°C+24h in water at 23°C; IEC 60167; IEC/EN 60893-2 6.3
Dielectric Constant	5.0 <br>@Thickness <=3.00 mm,<br> Frequency 50.0 Hz	5.0 <br>@Thickness <=0.118 in,<br> Frequency 50.0 Hz	96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
Dielectric Strength	0.600 kV/mm <br>@Thickness >=3.00 mm	15.2 kV/in <br>@Thickness >=0.118 in	24hr/23°C/50% RH+1hr/oil 90°C; Parallel; IEC 60245-1; IEC/EN 60893-2 6.1.3.2
	4.00 kV/mm <br>@Thickness 3.00 mm	102 kV/in <br>@Thickness 0.118 in	24hr/23°C/50% RH+1hr/oil 90°C; Perpendicular; IEC 60245-1; IEC/EN 60893-2 6.1.3.1
Dissipation Factor	0.050 <br>@Frequency 50.0 Hz	0.050 <br>@Frequency 50.0 Hz	96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
Comparative Tracking Index	100 V <br>@Thickness 3.00 mm	100 V <br>@Thickness 0.118 in	IEC 60112; IEC/EN 60893-2 6.4