Eastman Tenite 383A-10 Cellulose Acetate Propionate  (discontinued **)

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate Propionate, Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman Tenite 383A-10 Cellulose Acetate Propionate  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
10% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
Linear Mold Shrinkage, Flow 0.0020 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0060 in/in

@Thickness 0.126 in
Mechanical Properties Metric English Comments
Tensile Strength, Yield 34.0 MPa
4930 psi
50 mm/min
Elongation at Break 37 %
37 %
Elongation at Yield 4.0 %
4.0 %
Tensile Modulus 1.78 GPa
258 ksi
1mm/min
Charpy Impact Unnotched NB
NB
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
Charpy Impact, Notched 1.62 J/cm²
7.71 ft-lb/in²
0.780 J/cm²

@Temperature -30.0 °C
 3.71 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 93.0 µm/m-°C

@Temperature 20.0 °C
 51.7 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 137 µm/m-°C

@Temperature 20.0 °C
 76.1 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 93.0 °C
199 °F
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
Vicat Softening Point 92.0 °C
198 °F
Glass Transition Temp, Tg 105 °C
221 °F
Processing Properties Metric English Comments
Melt Temperature 240 - 250 °C
464 - 482 °F