Eastman Eastar EN010 Copolyester
| Category | Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | Eastman Chemical |
| Trade Name | Eastar |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eastman Eastar EN010 Copolyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Eastar copolyester EN010 is used primarily in molded thick wall European applications.Applications/UsesPackagingInjection moldingContainers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.20 mm |
0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ASTM D638 |
| Elongation at Break | 125 % | 125 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.44 GPa | 354 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Temperature -40.0 °C |
0.599 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| 0.540 J/cm @Temperature 23.0 °C |
1.01 ft-lb/in @Temperature 73.4 °F |
ASTM D256 | |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| 24.0 J/cm @Temperature -40.0 °C |
45.0 ft-lb/in @Temperature -40.0 °F |
ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 275 - 295 °C | 527 - 563 °F | |
| Mold Temperature | 10.0 - 30.0 °C | 50.0 - 86.0 °F | |
| Drying Temperature | 150 - 160 °C | 302 - 320 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1301-8456 PPS, linear, with glass fiber, PTFE, lubricant modified
- Specialty Coating Systems Parylene N Poly (P-Xylylene) Coating
- SABIC Innovative Plastics LNP STAT-LOY 63000CT PC+POLYESTER (Asia Pacific)
- Stir SpA SA 105/2 (PVC)
- EMS-Grivory Grivory® GV-5H black PA*-GF50
- Dow BETAMATE™ 7050 L Epoxy
- ExxonMobil Mobil Vactra 4
- 3M Scotch® 8621 Tear Strip Tape
- Resinlab® EP1305 Black Highly Toughened Urethane Modified Epoxy
Copyright © lookpolymers.com All Rights Reserved