Eagle Brass 301 Austenitic Stainless Steel, Full Hardened

Category	Metal , Ferrous Metal , Stainless Steel , T 300 Series Stainless Steel
Manufacturer	Eagle Brass Company
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Eagle Brass 301 Austenitic Stainless Steel, Full Hardened.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Type 301 is a chromium-nickel stainless steel that provides high strength and good ductility with chromium and nickel contents lowered to increase the work hardening range. This permits higher tensile strengths to be achieved by rolling with a lower loss of ductility. When this grade is cold worked it becomes more magnetic than other austenitic stainless steels. Typical uses include aircraft structural parts, diaphragms, utensils, automotive trim, and conveyor belts.Information provided by Eagle Brass Company

Physical Properties	Metric	English	Comments
Density	7.89 g/cc	0.285 lb/in³	As Annealed

Mechanical Properties	Metric	English	Comments
Tensile Strength	>= 1280 MPa	>= 185000 psi
Tensile Strength, Yield	>= 965 MPa	>= 140000 psi	0.2% Offset
Elongation at Break	>= 8.0 %	>= 8.0 %	in 2 inches
Tensile Modulus	193 GPa	28000 ksi

Thermal Properties	Metric	English	Comments
CTE, linear	18.7 µm/m-°C @Temperature 20.0 - 649 °C	10.4 µin/in-°F @Temperature 68.0 - 1200 °F
Thermal Conductivity	16.3 W/m-K	113 BTU-in/hr-ft²-°F

Component Elements Properties	Metric	English	Comments
Carbon, C	<= 0.15 %	<= 0.15 %
Chromium, Cr	16 - 18 %	16 - 18 %
Iron, Fe	74.775 - 78 %	74.775 - 78 %	Calculated as Balance
Manganese, Mn	<= 2.0 %	<= 2.0 %
Nickel, Ni	6.0 - 8.0 %	6.0 - 8.0 %
Phosphorous, P	<= 0.045 %	<= 0.045 %
Silicon, Si	<= 1.0 %	<= 1.0 %
Sulfur, S	<= 0.030 %	<= 0.030 %