POLYMER SEARCH

EMS-Grivory Grivory® BRZ 234/1 W PA6

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	EMS-Grivory (EMS-CHEMIE)
Trade Name	Grivory®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	EMS-Grivory Grivory® BRZ 234/1 W PA6.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Grilon BRZ 234/1 W is a modified polyamide 6, suitable for tube extrusion. Grilon BRZ 234/1 W is heat stabilized, shows a high flexibility and high impact strength. It is especially developed for the direct contact with automotive fuels.Information provided by EMS Grivory

Physical Properties	Metric	English	Comments
Density	1.12 g/cc	0.0405 lb/in³	ISO 1183

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	35.0 MPa	5080 psi	conditioned; ISO 527-1/-2
	40.0 MPa	5800 psi	dry; ISO 527-1/-2
Elongation at Break	>= 50 %	>= 50 %	dry; ISO 527-1/-2
	>= 50 %	>= 50 %	conditioned; ISO 527-1/-2
Tensile Modulus	0.380 GPa	55.1 ksi	conditioned; ISO 527-1/-2
	0.800 GPa	116 ksi	dry; ISO 527-1/-2
Charpy Impact Unnotched	NB	NB	dry; ISO 179/1eU
	NB	NB	conditioned; ISO 179/1eU
	NB @Temperature 30.0 °C	NB @Temperature 86.0 °F	dry; ISO 179/1eU
	NB @Temperature 30.0 °C	NB @Temperature 86.0 °F	conditioned; ISO 179/1eU
Charpy Impact, Notched	NB	NB	dry; ISO 179/1eA
	NB	NB	conditioned; ISO 179/1eA
	0.500 J/cm² @Temperature 30.0 °C	2.38 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	0.800 J/cm² @Temperature 30.0 °C	3.81 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU

Thermal Properties	Metric	English	Comments
Melting Point	215 °C	419 °F	10°C/min; ISO 11357-1/-3

Descriptive Properties	Value	Comments
Additives	Plasticizer
Automotive	Air intake sytems
	Cooling and climate control
Electricals & Electronics	Cables & Tubes
Form	Granules
Industry & Consumer goods	Hydraulics & Pneumatics
	Mechanical Engineering
	Power transmission
Processing	Other Extrusion
Product Attributes	Flexible
Special Characteristics	High impact or impact modified

Users viewing this material also viewed the following: