E-Polymers TEKAPPO® J910 10% Glass Fiber Reinforced M-PPO

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 10% Glass Filled
Manufacturer	E-Polymers Co. Ltd.
Trade Name	TEKAPPO®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	E-Polymers TEKAPPO® J910 10% Glass Fiber Reinforced M-PPO.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Modified PPO/PPE: TEKAPPO is a modified PPO/PPE, blending PPO with HIPS in order to improve HDT and processability. It displays various HDT range with halogen-free flammability, impact resistance and reinforced fiberglass. It shows high dimensional stability and rigidity used for housing and electrical parts.Information Provided by E-Polymers Co., Ltd.

Physical Properties	Metric	English	Comments
Specific Gravity	1.14 g/cc	1.14 g/cc	ASTM D792
Water Absorption	0.060 % @Time 86400 sec	0.060 % @Time 24.0 hour
Linear Mold Shrinkage	0.0020 cm/cm	0.0020 in/in
Linear Mold Shrinkage, Transverse	0.0050 cm/cm	0.0050 in/in

Mechanical Properties	Metric	English	Comments
Tensile Strength	73.575 MPa	10671 psi	ASTM D638
Elongation at Break	5.0 %	5.0 %	ASTM D638
Flexural Strength	98.1 MPa	14200 psi	ASTM D790
Flexural Modulus	3.4335 GPa	497.99 ksi	ASTM D790
Izod Impact, Notched	1.18 J/cm	2.20 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	123 °C	253 °F	ASTM D648
Flammability, UL94	HB	HB

Processing Properties	Metric	English	Comments
Melt Temperature	280 - 310 °C	536 - 590 °F
Mold Temperature	80.0 - 100 °C	176 - 212 °F