E-Polymers SEPAZ® C140GM 40% Glass Fiber/Mineral Reinforced LCP Resin

Category	Polymer , Thermoplastic , Liquid Crystal Polymer (LCP)
Manufacturer	E-Polymers Co. Ltd.
Trade Name	SEPAZ®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	E-Polymers SEPAZ® C140GM 40% Glass Fiber/Mineral Reinforced LCP Resin.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Liquid Crystal Polymer Resin: SEPAZ LCP resin has a unique structure and performance unthought of in a traditional plastics. Beside SEPAZ LCP takes the excels in all-around performance and molding productivity. SEPAZ LCP has a unique attribute in that the thinner the product becomes, the greater the mechanical strength. SEPAZ LCP finds uses in connectors, sensors and other electronic components and CD pick-up parts, and in copying machine and fax components in office and audio-visual equipment.Information Provided by E-Polymers Co., Ltd.

Physical Properties	Metric	English	Comments
Specific Gravity	1.73 g/cc	1.73 g/cc	ASTM D792
Water Absorption	0.020 % @Time 86400 sec	0.020 % @Time 24.0 hour
Linear Mold Shrinkage	0.0010 cm/cm	0.0010 in/in
Linear Mold Shrinkage, Transverse	0.0040 cm/cm	0.0040 in/in

Mechanical Properties	Metric	English	Comments
Tensile Strength	111.8 MPa	16220 psi	ASTM D638
Elongation at Break	1.5 %	1.5 %	ASTM D638
Flexural Strength	163.83 MPa	23762 psi	ASTM D790
Flexural Modulus	13.2 GPa	1910 ksi	ASTM D790
Izod Impact, Notched	0.0686 J/cm	0.129 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	335 °C	635 °F	ASTM D789
Deflection Temperature at 1.8 MPa (264 psi)	269 °C	516 °F	ASTM D648
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+14 ohm-cm	>= 1.00e+14 ohm-cm	ASTM D257
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	ASTM D257
Dielectric Constant	3.6 @Frequency 1.00e+6 Hz	3.6 @Frequency 1.00e+6 Hz	ASTM D150
Dissipation Factor	0.023 @Frequency 1.00e+6 Hz	0.023 @Frequency 1.00e+6 Hz	ASTM D150

Processing Properties	Metric	English	Comments
Melt Temperature	350 - 360 °C	662 - 680 °F
Mold Temperature	40.0 - 150 °C	104 - 302 °F