Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

DuPont Teijin Films Mylar® M45 Polyester Film, 50 Gauge (15 µm), PVDC Coated  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyester, TP , PVDC , Polyvinyl Dichloride (PVDC) Coated Polyester Film
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Teijin Films Mylar® M45 Polyester Film, 50 Gauge (15 µm), PVDC Coated  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by DuPont Packaging Polymers.A transparent polyester packaging film, dispersion coated on one side with a PVDC copolymer. The coating is an excellent moisture and oxygen barrier. M45 is designed to be combined with a sealant layer, locking in the PVDC coating. M45 can be surface or reverse printed with appropriately formulated inks, and can be combined with other webs by adhesive or extrusion laminating. The coated surface is particularly well suited for water based inks and adhesives.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
Average value for Mylar® films.
Moisture Vapor Transmission 0.0900 cc-mm/m²-24hr-atm
0.229 cc-mil/100 in²-24hr-atm
ASTM E96 Procedure E
Water Vapor Transmission 6.00 g/m²/day
0.386 g/100 in²/day
ASTM E96 Procedure E
Oxygen Transmission 0.0780 cc-mm/m²-24hr-atm
0.198 cc-mil/100 in²-24hr-atm
or 6 cc/m²-24hr-atm for the film. ASTM D3985
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 155 %
155 %
ASTM D882
Film Elongation at Break, TD 120 %
120 %
ASTM D882
Modulus of Elasticity 3.45 GPa
500 ksi
(stiffness), ASTM D882
Tear Strength Test 300
300
Graves, g; ASTM D1004
Film Tensile Strength at Break, MD 152 MPa
22000 psi
ASTM D882
Film Tensile Strength at Break, TD 179 MPa
26000 psi
ASTM D882
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Not cleared by FDA for food temperatures above this temperature.
Shrinkage 2.2 %

@Temperature 150 °C,
Time 1800 sec
2.2 %

@Temperature 302 °F,
Time 0.500 hour
Film shrinkage in oven.
Optical Properties Metric English Comments
Haze 7.0 %
7.0 %
ASTM D1003
Gloss 130 %
130 %
20°; ASTM D2457
Transmission, Visible 70 %
70 %
% Clarity; ASTM D1746
Copyright © lookpolymers.com All Rights Reserved