DuPont Teijin Films Melinex® 516D Polyester Film
| Category | Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film |
| Manufacturer | DuPont Teijin Films (DTF) |
| Trade Name | Melinex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Teijin Films Melinex® 516D Polyester Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A high clarity film which is two side pretreated for slip to combine good handling properties with high clarity and brilliance.Information provided by DuPont.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 96.5 MPa | 14000 psi | ASTM D882A |
| Film Tensile Strength at Yield, TD | 100 MPa | 14500 psi | ASTM D882A |
| Film Elongation at Break, MD | 180 % | 180 % | ASTM D882A |
| Film Elongation at Break, TD | 120 % | 120 % | ASTM D882A |
| Coefficient of Friction, Dynamic | 0.45 | 0.45 | A-B; ASTM D1894 |
| Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
| Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 2.5 % @Temperature 190 °C, Time 300 sec |
2.5 % @Temperature 374 °F, Time 0.0833 hour |
Unrestrained |
| Shrinkage, TD | 0.40 % @Temperature 190 °C, Time 300 sec |
0.40 % @Temperature 374 °F, Time 0.0833 hour |
Unrestrained |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 88.2 % @Thickness 0.163 mm |
88.2 % @Thickness 0.00640 in |
TLT; ASTM D1003 |
| 88.3 % @Thickness 0.0940 mm |
88.3 % @Thickness 0.00370 in |
TLT; ASTM D1003 | |
| 88.3 % @Thickness 0.112 mm |
88.3 % @Thickness 0.00440 in |
TLT; ASTM D1003 |
Users viewing this material also viewed the following:
- Nyco NYAD® MD325 Wollastonite
- SABIC Innovative Plastics LNP KONDUIT PX10322 PA 6 (Asia Pacific)
- DuPont Performance Polymers Crastin® SK602 BK851 PBT (Unverified Data**)
- Overview of materials for Phenolic, Novolac, Glass Filled
- H.C. Starck Amperit® 544.059 Dense Coated Tungsten Carbide-Nickel 83-17 (WC-Ni)
- A. Schulman POLYFLAM™ RPP 1174 Talc Filled, Homopolymer Polypropylene
- Arlon T1020-R004-## 0.020" Self-Fusing Silicone Rubber Tape
- Asahi Glass Fluon® L173J PTFE Lubricant
- Unitika EX-1020K PA6, Dry
Copyright © lookpolymers.com All Rights Reserved