DuPont™ Surlyn® 6320 Magnesium Ionomer

Category	Polymer , Thermoplastic , Ionomer
Manufacturer	DuPont
Trade Name	Surlyn®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont™ Surlyn® 6320 Magnesium Ionomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Surlyn® 6320 is a magnesium ionomer thermoplastic resin. It is available for use in conventional extrusion and injection equipment, to create various sheets or shapes. Surlyn® 6320 thermoplastic resin is an advanced ethylene/acid/acrylate terpolymer, in which some of the MAA acid groups have been partially neutralized with magnesium ions.

Physical Properties	Metric	English	Comments
Density	0.950 g/cc	0.0343 lb/in³	ASTM D792, ISO 1183
Melt Flow	1.0 g/10 min @Load 2.16 kg, Temperature 190 °C	1.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238, ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	43	43	ASTM D2240, ISO 868
Tensile Strength at Break	23.4 MPa @Temperature 23.0 °C	3390 psi @Temperature 73.4 °F	ASTM D638, ISO 527-2
Elongation at Break	530 % @Temperature 23.0 °C	530 % @Temperature 73.4 °F	ASTM D638, ISO 527-2
Flexural Modulus	0.0531 GPa @Temperature 23.0 °C	7.70 ksi @Temperature 73.4 °F	ASTM D790

Thermal Properties	Metric	English	Comments
Melting Point	34.0 °C	93.2 °F	Freezing Point; ASTM D3418, ISO 3146
	70.0 °C	158 °F	ASTM D3418, ISO 3146
Vicat Softening Point	49.0 °C	120 °F	ASTM D1525, ISO 306

Processing Properties	Metric	English	Comments
Processing Temperature	<= 285 °C	<= 545 °F
Melt Temperature	185 - 285 °C	365 - 545 °F	Extrusion Coating