DuPont Performance Polymers Zytel® PLUS PLS95G40DH1T BK261 Nylon  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon
Manufacturer DuPont Performance Polymers
Trade Name Zytel® PLUS
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® PLUS PLS95G40DH1T BK261 Nylon  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zytel® PLS95G40DH1T is a 40% GR impact modified PA, made with SHIELD technology, its superior heat & oil resistance combined with the "stone impact resistance" makes it ideal choice for use in severe environments exposed to heat and oil.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
DAM; ISO 1183
Filler Content 40 %
40 %
DAM
Linear Mold Shrinkage, Flow 0.0035 cm/cm
0.0035 in/in
DAM; 60x60x2mm; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0075 cm/cm
0.0075 in/in
Normal; DAM; 60x60x2mm; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 175 MPa

@Temperature 23.0 °C
 25400 psi

@Temperature 73.4 °F
 DAM; ISO 527
Tensile Stress 8.48 MPa

@Strain 0.100 %,
Temperature 150 °C
 1230 psi

@Strain 0.100 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
9.37 MPa

@Strain 0.100 %,
Temperature 100 °C
 1360 psi

@Strain 0.100 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
13.38 MPa

@Strain 0.100 %,
Temperature 23.0 °C
 1941 psi

@Strain 0.100 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
13.65 MPa

@Strain 0.200 %,
Temperature 150 °C
 1980 psi

@Strain 0.200 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
13.68 MPa

@Strain 0.100 %,
Temperature -40.0 °C
 1984 psi

@Strain 0.100 %,
Temperature -40.0 °F
 DAM; ISO 11403-1/-2
15.46 MPa

@Strain 0.200 %,
Temperature 100 °C
 2242 psi

@Strain 0.200 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
17.41 MPa

@Strain 0.300 %,
Temperature 150 °C
 2525 psi

@Strain 0.300 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
20.02 MPa

@Strain 0.400 %,
Temperature 150 °C
 2904 psi

@Strain 0.400 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
20.36 MPa

@Strain 0.300 %,
Temperature 100 °C
 2953 psi

@Strain 0.300 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
23.84 MPa

@Strain 0.400 %,
Temperature 100 °C
 3458 psi

@Strain 0.400 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
23.91 MPa

@Strain 0.500 %,
Temperature 150 °C
 3468 psi

@Strain 0.500 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
25.48 MPa

@Strain 0.200 %,
Temperature 23.0 °C
 3696 psi

@Strain 0.200 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
26.55 MPa

@Strain 0.200 %,
Temperature -40.0 °C
 3851 psi

@Strain 0.200 %,
Temperature -40.0 °F
 DAM; ISO 11403-1/-2
26.56 MPa

@Strain 0.600 %,
Temperature 150 °C
 3852 psi

@Strain 0.600 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
29.0 MPa

@Strain 0.700 %,
Temperature 150 °C
 4210 psi

@Strain 0.700 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
29.22 MPa

@Strain 0.500 %,
Temperature 100 °C
 4238 psi

@Strain 0.500 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
31.14 MPa

@Strain 0.800 %,
Temperature 150 °C
 4516 psi

@Strain 0.800 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
32.91 MPa

@Strain 0.600 %,
Temperature 100 °C
 4773 psi

@Strain 0.600 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
33.05 MPa

@Strain 0.900 %,
Temperature 150 °C
 4794 psi

@Strain 0.900 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
34.86 MPa

@Strain 1.00 %,
Temperature 150 °C
 5056 psi

@Strain 1.00 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
36.34 MPa

@Strain 0.700 %,
Temperature 100 °C
 5271 psi

@Strain 0.700 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
36.53 MPa

@Strain 1.10 %,
Temperature 150 °C
 5298 psi

@Strain 1.10 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
36.78 MPa

@Strain 0.300 %,
Temperature 23.0 °C
 5334 psi

@Strain 0.300 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
37.79 MPa

@Strain 1.20 %,
Temperature 150 °C
 5481 psi

@Strain 1.20 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
38.03 MPa

@Strain 0.300 %,
Temperature -40.0 °C
 5516 psi

@Strain 0.300 %,
Temperature -40.0 °F
 DAM; ISO 11403-1/-2
38.78 MPa

@Strain 0.800 %,
Temperature 100 °C
 5625 psi

@Strain 0.800 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
39.4 MPa

@Strain 1.30 %,
Temperature 150 °C
 5710 psi

@Strain 1.30 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
40.83 MPa

@Strain 1.40 %,
Temperature 150 °C
 5922 psi

@Strain 1.40 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
41.92 MPa

@Strain 0.900 %,
Temperature 100 °C
 6080 psi

@Strain 0.900 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
42.1 MPa

@Strain 1.50 %,
Temperature 150 °C
 6110 psi

@Strain 1.50 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
43.27 MPa

@Strain 1.60 %,
Temperature 150 °C
 6276 psi

@Strain 1.60 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
44.37 MPa

@Strain 1.70 %,
Temperature 150 °C
 6435 psi

@Strain 1.70 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
44.59 MPa

@Strain 1.00 %,
Temperature 100 °C
 6467 psi

@Strain 1.00 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
45.43 MPa

@Strain 1.80 %,
Temperature 150 °C
 6589 psi

@Strain 1.80 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
45.46 MPa

@Strain 0.400 %,
Temperature 23.0 °C
 6593 psi

@Strain 0.400 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
46.29 MPa

@Strain 1.90 %,
Temperature 150 °C
 6714 psi

@Strain 1.90 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
47.03 MPa

@Strain 1.10 %,
Temperature 100 °C
 6821 psi

@Strain 1.10 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
47.21 MPa

@Strain 2.00 %,
Temperature 150 °C
 6847 psi

@Strain 2.00 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
48.15 MPa

@Strain 2.10 %,
Temperature 150 °C
 6984 psi

@Strain 2.10 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
48.47 MPa

@Strain 0.400 %,
Temperature -40.0 °C
 7030 psi

@Strain 0.400 %,
Temperature -40.0 °F
 DAM; ISO 11403-1/-2
49.01 MPa

@Strain 2.20 %,
Temperature 150 °C
 7108 psi

@Strain 2.20 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
49.06 MPa

@Strain 1.20 %,
Temperature 100 °C
 7116 psi

@Strain 1.20 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
49.83 MPa

@Strain 2.30 %,
Temperature 150 °C
 7227 psi

@Strain 2.30 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
50.63 MPa

@Strain 2.40 %,
Temperature 150 °C
 7343 psi

@Strain 2.40 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
50.99 MPa

@Strain 1.30 %,
Temperature 100 °C
 7395 psi

@Strain 1.30 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
51.39 MPa

@Strain 2.50 %,
Temperature 150 °C
 7454 psi

@Strain 2.50 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
52.13 MPa

@Strain 2.60 %,
Temperature 150 °C
 7561 psi

@Strain 2.60 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
52.83 MPa

@Strain 2.70 %,
Temperature 150 °C
 7662 psi

@Strain 2.70 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
52.97 MPa

@Strain 1.40 %,
Temperature 100 °C
 7683 psi

@Strain 1.40 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
53.45 MPa

@Strain 2.80 %,
Temperature 150 °C
 7752 psi

@Strain 2.80 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
54.08 MPa

@Strain 2.90 %,
Temperature 150 °C
 7844 psi

@Strain 2.90 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
54.71 MPa

@Strain 3.00 %,
Temperature 150 °C
 7935 psi

@Strain 3.00 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
54.89 MPa

@Strain 1.50 %,
Temperature 100 °C
 7961 psi

@Strain 1.50 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
55.36 MPa

@Strain 3.10 %,
Temperature 150 °C
 8029 psi

@Strain 3.10 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
55.95 MPa

@Strain 3.20 %,
Temperature 150 °C
 8115 psi

@Strain 3.20 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
56.43 MPa

@Strain 3.30 %,
Temperature 150 °C
 8184 psi

@Strain 3.30 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
56.68 MPa

@Strain 1.60 %,
Temperature 100 °C
 8221 psi

@Strain 1.60 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
57.07 MPa

@Strain 3.40 %,
Temperature 150 °C
 8277 psi

@Strain 3.40 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
57.6 MPa

@Strain 3.50 %,
Temperature 150 °C
 8350 psi

@Strain 3.50 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2