DuPont Performance Polymers Rynite® FR530 BK507 PET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Rynite® FR530 BK507 PET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Rynite® FR530 BK507 is a 30% glass reinforced, flame retardant, modified polyethylene terephthalate resin.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.68 g/cc
0.0607 lb/in³
ISO 1183
Filler Content 30 %
30 %
Linear Mold Shrinkage, Flow 0.0020 cm/cm

@Thickness 2.00 mm
 0.0020 in/in

@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm

@Thickness 2.00 mm
 0.0080 in/in

@Thickness 0.0787 in
 ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 43.0 MPa

@Temperature 150 °C
 6240 psi

@Temperature 302 °F
 ISO 527
67.0 MPa

@Temperature 90.0 °C
 9720 psi

@Temperature 194 °F
 ISO 527
130 MPa

@Temperature 23.0 °C
 18900 psi

@Temperature 73.4 °F
 ISO 527
172 MPa

@Temperature -40.0 °C
 24900 psi

@Temperature -40.0 °F
 ISO 527
Elongation at Break 1.8 %

@Temperature -40.0 °C
 1.8 %

@Temperature -40.0 °F
 ISO 527
1.9 %

@Temperature 23.0 °C
 1.9 %

@Temperature 73.4 °F
 ISO 527
3.5 %

@Temperature 90.0 °C
 3.5 %

@Temperature 194 °F
 ISO 527
4.0 %

@Temperature 150 °C
 4.0 %

@Temperature 302 °F
 ISO 527
Tensile Modulus 3.65 GPa

@Temperature 150 °C
 529 ksi

@Temperature 302 °F
 ISO 527
5.90 GPa

@Temperature 90.0 °C
 856 ksi

@Temperature 194 °F
 ISO 527
11.3 GPa

@Temperature 23.0 °C
 1640 ksi

@Temperature 73.4 °F
 ISO 527
12.0 GPa

@Temperature -40.0 °C
 1740 ksi

@Temperature -40.0 °F
 ISO 527
Flexural Strength 69.0 MPa

@Temperature 150 °C
 10000 psi

@Temperature 302 °F
 ISO 178
107 MPa

@Temperature 90.0 °C
 15500 psi

@Temperature 194 °F
 ISO 178
200 MPa

@Temperature 23.0 °C
 29000 psi

@Temperature 73.4 °F
 ISO 178
262 MPa

@Temperature -40.0 °C
 38000 psi

@Temperature -40.0 °F
 ISO 178
Flexural Modulus 2.65 GPa

@Temperature 150 °C
 384 ksi

@Temperature 302 °F
 ISO 178
4.65 GPa

@Temperature 90.0 °C
 674 ksi

@Temperature 194 °F
 ISO 178
10.5 GPa

@Temperature 23.0 °C
 1520 ksi

@Temperature 73.4 °F
 ISO 178
11.0 GPa

@Temperature -40.0 °C
 1600 ksi

@Temperature -40.0 °F
 ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Temperature -40.0 °C
 3.81 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1A
8.50 kJ/m²

@Temperature 23.0 °C
 4.04 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1A
Izod Impact, Unnotched (ISO) 34.0 kJ/m²

@Temperature -40.0 °C
 16.2 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1U
35.0 kJ/m²

@Temperature -30.0 °C
 16.7 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1U
40.0 kJ/m²

@Temperature 23.0 °C
 19.0 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1U
Charpy Impact Unnotched 3.00 J/cm²

@Temperature -40.0 °C
 14.3 ft-lb/in²

@Temperature -40.0 °F
 ISO 179/1eU
3.50 J/cm²

@Temperature -30.0 °C
 16.7 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
4.00 J/cm²

@Temperature 23.0 °C
 19.0 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²

@Temperature -40.0 °C
 3.81 ft-lb/in²

@Temperature -40.0 °F
 ISO 179/1eA
0.800 J/cm²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
0.900 J/cm²

@Temperature 23.0 °C
 4.28 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature -40.0 - 23.0 °C
 278 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
500 µm/m-°C

@Temperature 23.0 - 55.0 °C
 278 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
500 µm/m-°C

@Temperature 55.0 - 160 °C
 278 µin/in-°F

@Temperature 131 - 320 °F
 ISO 11359-1/-2
CTE, linear, Transverse to Flow 73.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
 40.6 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
90.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
121 µm/m-°C

@Temperature 55.0 - 160 °C
 67.2 µin/in-°F

@Temperature 131 - 320 °F
 ISO 11359-1/-2
Melting Point 252 °C
486 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 243 °C
469 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 220 °C
428 °F
ISO 75-1/-2
UL RTI, Electrical 155 °C

@Thickness 0.350 mm
 311 °F

@Thickness 0.0138 in
 UL 746B
155 °C

@Thickness 0.750 mm
 311 °F

@Thickness 0.0295 in
 UL 746B
155 °C

@Thickness 1.50 mm
 311 °F

@Thickness 0.0591 in
 UL 746B
155 °C

@Thickness 2.00 mm
 311 °F

@Thickness 0.0787 in
 UL 746B
155 °C

@Thickness 3.00 mm
 311 °F

@Thickness 0.118 in
 UL 746B
UL RTI, Mechanical with Impact 155 °C

@Thickness 2.00 mm
 311 °F

@Thickness 0.0787 in
 UL 746B
155 °C

@Thickness 3.00 mm
 311 °F

@Thickness 0.118 in
 UL 746B
155 °C

@Thickness 1.50 mm
 311 °F

@Thickness 0.0591 in
 UL 746B
155 °C

@Thickness 0.750 mm
 311 °F

@Thickness 0.0295 in
 UL 746B
UL RTI, Mechanical without Impact 155 °C

@Thickness 0.750 mm
 311 °F

@Thickness 0.0295 in
 UL 746B
155 °C

@Thickness 1.50 mm
 311 °F

@Thickness 0.0591 in
 UL 746B
155 °C

@Thickness 2.00 mm
 311 °F

@Thickness 0.0787 in
 UL 746B
155 °C

@Thickness 3.00 mm
 311 °F

@Thickness 0.118 in
 UL 746B
Flammability, UL94 V-0

@Thickness 2.00 mm
 V-0

@Thickness 0.0787 in
 UL94
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL94
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
 UL94
V-0

@Thickness 0.350 mm
 V-0

@Thickness 0.0138 in
 UL94
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
 IEC 60695-11-10
Electrical Properties Metric English Comments
Comparative Tracking Index 225 V

@Temperature 23.0 °C
 225 V

@Temperature 73.4 °F
 IEC 60112
250 V

@Temperature 23.0 °C
 250 V

@Temperature 73.4 °F
 UL 746A
250 - 400 V

@Temperature 23.0 °C
 250 - 400 V

@Temperature 73.4 °F
 UL 746A