- DuPont Performance Polymers Hytrel® G4078 NC010 Polyester Elastomer TPC-ET (Unverified Data**)
DuPont Performance Polymers Hytrel® G4078 NC010 Polyester Elastomer TPC-ET (Unverified Data**)
| Category | Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Hytrel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Hytrel® G4078 NC010 Polyester Elastomer TPC-ET
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
40 Shore D Standard Performance Polyester Elastomer with Non-discoloring StabilizerInformation provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | |
| 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 | |
| Water Absorption | 6.5 % @Thickness 2.00 mm |
6.5 % @Thickness 0.0787 in |
Sim. to ISO 62 |
| Moisture Absorption | 0.700 % @Thickness 2.00 mm |
0.700 % @Thickness 0.0787 in |
Sim. to ISO 62 |
| Water Absorption at Saturation | 3.4 % | 3.4 % | Immersion 24h; ASTM D570 |
| Water Vapor Transmission | 2000 g/m²/day @Thickness 0.0250 mm |
129 g/100 in²/day @Thickness 0.000984 in |
23°C/85%r.h.; DIS 15106-1/-2 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ISO 294-4 2577 |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | ISO 294-4 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 33 | 33 | 15s; ISO 868 |
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ISO 527-1/-2 |
| Tensile Stress | 2.50 MPa @Strain 5.00 % |
363 psi @Strain 5.00 % |
ISO 527-1/-2 |
| 4.20 MPa @Strain 10.0 % |
609 psi @Strain 10.0 % |
ISO 527-1/-2 | |
| 8.50 MPa @Strain 50.0 % |
1230 psi @Strain 50.0 % |
ISO 527-1/-2 | |
| Elongation at Break | 220 % | 220 % | ISO 527-1/-2 |
| 250 % | 250 % | Nominal; ISO 527-1/-2 | |
| Tensile Modulus | 0.0550 GPa | 7.98 ksi | ISO 527-1/-2 |
| Charpy Impact, Notched | NB | NB | ISO 179/1eA |
| Tear Strength | 120 kN/m | 685 pli | normal; ISO 34-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 170 °C | 338 °F | 10°C/min; ISO 11357-1/-3 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Delivery Form | Pellets | |
| Part Marking Code | >TPC-ET< | ISO 11469 |
| Processing | Casting | |
| Film Extrusion | ||
| Injection Moulding | ||
| Profile Extrusion | ||
| Sheet Extrusion | ||
| Thermoforming | ||
| Regional Availability | Asia Pacific | |
| Europe | ||
| Global | ||
| Near East/Africa | ||
| North America | ||
| South and Central America | ||
| Resin Identification | TPC-ET | ISO 1043 |
| Type of extrusion | blown |
Users viewing this material also viewed the following:
- Overview of materials for Polyetheretherketone, PTFE Filled
- Plenco 4759 Phenolic, Granular, Injection Molded (discontinued **)
- LyondellBasell Pro-fax PD702NW Polypropylene Homopolymer, Nucleated/Antistat
- MetalTek MTEK 375 Aluminum Bronze
- A. Schulman POLYBATCH™ White P8555 SC Concentrate Based In Random Copolymer Polypropylene
- Formosa Plastics Formolene® 5100H Extrusion processing Polypropylene
- Arlon 44566R020 0.020" (0.508 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Asia International Enterprise (Hong Kong) 60T6 Nylon 66, 30% Filled
- Trelleborg Commercial Neoprene® C433 Chloroprene
Copyright © lookpolymers.com All Rights Reserved