- DuPont Performance Polymers Hytrel® G3548 NC010 Polyester Elastomer TPC-ET (Unverified Data**)
DuPont Performance Polymers Hytrel® G3548 NC010 Polyester Elastomer TPC-ET (Unverified Data**)
| Category | Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Hytrel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Hytrel® G3548 NC010 Polyester Elastomer TPC-ET
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
35 Shore D Standard Performance Polyester Elastomer with Non-discoloring StabilizerInformation provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Water Absorption | 12 % @Thickness 2.00 mm |
12 % @Thickness 0.0787 in |
Sim. to ISO 62 |
| Moisture Absorption | 0.800 % @Thickness 2.00 mm |
0.800 % @Thickness 0.0787 in |
Sim. to ISO 62 |
| Water Absorption at Saturation | 6.9 % | 6.9 % | Immersion 24h; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4 2577 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 24 | 24 | 15s; ISO 868 |
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO 527-1/-2 |
| Tensile Stress | 1.50 MPa @Strain 5.00 % |
218 psi @Strain 5.00 % |
ISO 527-1/-2 |
| 2.50 MPa @Strain 10.0 % |
363 psi @Strain 10.0 % |
ISO 527-1/-2 | |
| 6.00 MPa @Strain 50.0 % |
870 psi @Strain 50.0 % |
ISO 527-1/-2 | |
| Elongation at Break | 190 % | 190 % | ISO 527-1/-2 |
| 200 % | 200 % | Nominal; ISO 527-1/-2 | |
| Tensile Modulus | 0.0250 GPa | 3.63 ksi | ISO 527-1/-2 |
| Flexural Modulus | 0.0250 GPa | 3.63 ksi | ISO 178 |
| Charpy Impact, Notched | NB | NB | ISO 179/1eA |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
ISO 179/1eA | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eA | |
| Tear Strength | 60.0 kN/m | 342 pli | parallel; ISO 34-1 |
| 80.0 kN/m | 456 pli | normal; ISO 34-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 157 °C | 315 °F | 10°C/min; ISO 11357-1/-3 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Delivery Form | Pellets | |
| Part Marking Code | >TPC-ET< | ISO 11469 |
| Processing | Film Extrusion | |
| Injection Moulding | ||
| Other Extrusion | ||
| Profile Extrusion | ||
| Regional Availability | Asia Pacific | |
| Europe | ||
| Global | ||
| Near East/Africa | ||
| North America | ||
| South and Central America | ||
| Resin Identification | TPC-ET | ISO 1043 |
Users viewing this material also viewed the following:
- GrafTech eGRAF® SPREADERSHIELD™ SS400 Graphite
- Fiberfil® PP-15/T/10/20 Polypropylene Homopolymer, 22% Talc Filled
- Saint-Gobain Chemfab® SlipGrip™ 6 PTFE/Silicone Coated Fiberglass Fabric
- A. Schulman LP390-01 Narrow Molecular Weight Copolymer
- Williams Advanced Alloys WS295 Solder
- Eurotec® Tecolen® CP10 GR10 NL PPCP, 10% glass fiber reinforced, natural
- C.O.I.M. EXTER S® S 103 L Orthophthalic Resin
- Solvay Specialty Polymers Diofan® A 036 Polyvinylidene Chloride (PVDC) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved