DuPont Performance Polymers Hytrel® 4056P Polyester Elastomer TPC-ET (Unverified Data**)
| Category | Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Hytrel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Hytrel® 4056P Polyester Elastomer TPC-ET
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
40 Shore D High Performance Polyester Elastomer in Powder FormInformation provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
cm³/10min; ISO 1133 |
| 5.6 g/10 min @Load 2.16 kg, Temperature 190 °C |
5.6 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 37 | 37 | 15s; ISO 868 |
| <= 43 | <= 43 | ISO 868 | |
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ISO 527-1/-2 |
| Tensile Stress | 2.40 MPa @Strain 5.00 % |
348 psi @Strain 5.00 % |
ISO 527-1/-2 |
| 4.60 MPa @Strain 10.0 % |
667 psi @Strain 10.0 % |
ISO 527-1/-2 | |
| 8.40 MPa @Strain 50.0 % |
1220 psi @Strain 50.0 % |
ISO 527-1/-2 | |
| Elongation at Break | >= 300 % | >= 300 % | ISO 527-1/-2 |
| 500 % | 500 % | Nominal; ISO 527-1/-2 | |
| Flexural Modulus | 0.0640 GPa | 9.28 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | NB | NB | ISO 179/1eA |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eA | |
| Tensile Impact Strength | 230 kJ/m² | 109 ft-lb/in² | notched; ISO 8256/1 |
| Tensile Creep Modulus, 1 hour | 54.0 MPa @Time 3600 sec |
7830 psi @Time 1.00 hour |
ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 40.0 MPa @Time 3.60e+6 sec |
5800 psi @Time 1000 hour |
ISO 899-1 |
| Tear Strength | 96.0 kN/m | 548 pli | normal; ISO 34-1 |
| 102 kN/m | 582 pli | parallel; ISO 34-1 | |
| Abrasion | 200 | 200 | mm³; ISO 4649 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 152 °C | 306 °F | 10°C/min; ISO 11357-1/-3 |
| Glass Transition Temp, Tg | -50.0 °C | -58.0 °F | 10°C/min; ISO 11357-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Delivery Form | Powder | |
| Processing | Thermoforming | |
| Regional Availability | Asia Pacific | |
| Europe | ||
| Global | ||
| Near East/Africa | ||
| North America | ||
| South and Central America | ||
| Resin Identification | TPC-ET | ISO 1043 |
| Special Characteristics | Light stabilised or stable to light |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CM6220 PC (Asia Pacific)
- Michelman® Michem® Guard 350 Nonionic, Fischer-Tropsch dispersion
- Schott N-ZK7 Glass
- Samsung Cheil Industries Starex® LX-0971 S ABS, Unreinforced Metallic-Look
- Sumitomo Bakelite Durez® 31735 Phenolic, Injection Grade
- Sumitomo Chemical ESPOLEX® 820 Thermoplastic Elastomer
- Polyplastics Duranex® HN7315 Polybutylene Terephthalate (PBT), Low warpage, 15% GF filled
- Hexcel® HexWeb® CR III 5/32-5056-.001 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Arlon 55606R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Multibase Multibatch® MP 53735 Injection Molding
Copyright © lookpolymers.com All Rights Reserved