DuPont Nucrel® 699 Ethylene-Methacrylic Acid Copolymer Resin

Category	Polymer , Thermoplastic , Ethylene Methyl Acrylate
Manufacturer	DuPont Packaging and Industrial Polymers
Trade Name	Nucrel®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Nucrel® 699 Ethylene-Methacrylic Acid Copolymer Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Nucrel® 599 is a tough, lightweight, easily processed ethylene copolymer resin. This resin is inherently flexible without the need for plasticizers. The resin can be pigmented, UV-stabilized for exterior applications and painted or plated for special decorative effects.Typical Applications: Ink modificationAdhesive componentSpecial adhesive filmsFeatures: Higher deflection temperatureGood adhesion to metals and polar substratesInformation provided by DuPont.

Physical Properties	Metric	English	Comments
Density	0.940 g/cc	0.0340 lb/in³	ASTM D792
Melt Index of Compound	95 g/10 min @Load 2.16 kg, Temperature 190 °C	95 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	46	46	Initial (peak) hardness; ASTM D2240
Tensile Strength at Break	15.2 MPa	2200 psi	Type IV specimen, compression molded, crosshead speed 2 in/min; ASTM D638
Elongation at Break	560 %	560 %	Type IV specimen, compression molded, crosshead speed 2 in/min; ASTM D638
Flexural Modulus	0.0683 GPa	9.91 ksi	ASTM D790
Izod Impact, Notched	NB	NB	ASTM D256
Tensile Impact Strength	491 kJ/m²	234 ft-lb/in²	At 23°C; ASTM D1822S
	288 kJ/m² @Temperature -40.0 °C	137 ft-lb/in² @Temperature -40.0 °F	ASTM D1822S

Thermal Properties	Metric	English	Comments
Melting Point	80.0 - 94.0 °C	176 - 201 °F	ASTM D3418(DSC)
Vicat Softening Point	65.0 °C	149 °F	ASTM D1525

Processing Properties	Metric	English
Zone 1	160 °C	320 °F
Zone 2	182 °C	360 °F
Zone 3	193 °C	379 °F
Zone 4	204 °C	399 °F
Zone 5	204 °C	399 °F
Die Temperature	204 °C	400 °F
Melt Temperature	149 - 232 °C	300 - 450 °F

Descriptive Properties	Value	Comments
Methacrylic Acid Content	11 wt.%	DuPont Method

Users viewing this material also viewed the following: