- Ethylene-Methyl Acrylate Copolymer, Molding Grade
- DuPont Elvaloy® 1209 AC Ethylene and 9% Methyl Acrylate Copolymer
DuPont Elvaloy® 1209 AC Ethylene and 9% Methyl Acrylate Copolymer
| Category | Polymer , Film , Thermoplastic , Ethylene Methyl Acrylate , Ethylene-Methyl Acrylate Copolymer, Molding Grade |
| Manufacturer | DuPont Packaging and Industrial Polymers |
| Trade Name | Elvaloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Elvaloy® 1209 AC Ethylene and 9% Methyl Acrylate Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Elvaloy® 1209 AC is intended for film coextrusion and injection molding. It can be recommended in film applications where softness, flexibility and excellent sealing properties are needed.Elvaloy® 1209 AC is easily processed on standard equipment used for low density polyethylene.Information provided by DuPont.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.927 g/cc | 0.0335 lb/in³ | ASTM D792 - ISO 1183 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 - ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 98 | 98 | ASTM D2240 - ISO 868 |
| Hardness, Shore D | 47 | 47 | ASTM D2240 - ISO 868 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | 500 mm/min; ASTM D638 - ISO 527-2 |
| Elongation at Break | 700 % | 700 % | 500 mm/min; ASTM D638 - ISO 527-2 |
| Tensile Modulus | 0.0800 GPa | 11.6 ksi | 1 mm/min; ASTM D638 - ISO 527-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 101 °C | 214 °F | By DSC; ASTM D3418 - ISO 3146 |
| Vicat Softening Point | 70.0 °C | 158 °F | A<sub>50</sub> (10N); ASTM D1525 - ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 150 °C | 302 °F | Extrusion lamination and extrusion coating |
| 150 °C | 302 °F | Cast film | |
| 150 °C | 302 °F | Blown film | |
| Middle Barrel Temperature | 160 °C | 320 °F | Blown film |
| 210 °C | 410 °F | Cast film | |
| 220 °C | 428 °F | Extrusion lamination | |
| Front Barrel Temperature | 170 °C | 338 °F | Blown film |
| 250 °C | 482 °F | Cast film | |
| 290 °C | 554 °F | Extrusion lamination | |
| Adapter Temperature | 180 °C | 356 °F | Blown film |
| 250 °C | 482 °F | Cast Film | |
| 290 °C | 554 °F | Extrusion lamination | |
| Die Temperature | 180 °C | 356 °F | Blown film |
| 250 °C | 482 °F | Cast film | |
| 290 °C | 554 °F | Extrusion lamination |
| Descriptive Properties | Value | Comments |
|---|---|---|
| MA-Content | 9 wt.% | DuPont Method |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8751R (UF) Synthetic Oil
- SABIC Innovative Plastics Lexan® CFR7630 PC COPOLYMER (Asia Pacific)
- Lubrizol Advanced Materials Pearlstick® 49-46/23 Linear Thermoplastic Polyurethane Elastomer (discontinued **
- Mallard Creek Polymers Rovene® 6117 Acrylic Emulsion
- Momentive Performance Materials Siloprenâ„¢ LSR 2670 Liquid Silicone Rubber - Fast Cure / High Tear
- Styron MAGNUMâ„¢ 3904 Smooth Acrylonitrile Butadiene Styrene (ABS) Resin
- Teknor Apex Telcar® TL-1431F Thermoplastic Elastomer
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 60 PHR N550 (FEF) Filler
- Diamond Polymers ABS 3501
Copyright © lookpolymers.com All Rights Reserved