Dow Nordel® IP 5565 Dense Extruded Profile
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Dow Chemical |
| Trade Name | Nordel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Nordel® IP 5565 Dense Extruded Profile.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FormulationNordel® IP 5565
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 73 @Temperature 100 °C |
73 @Temperature 212 °F |
ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 73 | 73 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 10.5 MPa | 1520 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 344 % | 344 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 50% Modulus | 0.00240 GPa | 0.348 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00440 GPa | 0.638 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.00760 GPa | 1.10 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.00930 GPa | 1.35 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 31.6 kN/m | 180 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 82 % @Temperature 125 °C |
82 % @Temperature 257 °F |
Pellets cured MDR t'95 + 15 min, 70 hr; Method B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -45.0 °C | -49.0 °F | Temperature Retraction, TR-10 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion 87548 AS Polyvinyl Chloride, Rigid (PVC, Rigid)
- Polimeri Europa Europrene Latice® 405 Carboxylated Styrene - Butadiene Copolymer
- Polymer Resources AC-GP2 Acetal Copolymer, Medium Flow
- Saint-Gobain Chemfab® 3 High-Performance PTFE-Coated Glass
- Styrolution Terblend® N NM-12 ABS/PA6 (Dry)
- Wellman Wellamid® MR409 22H-N 40% Mineral Reinforced Nylon 66, Heat Stabilized
- Wingate Alloys Champaloy Clad Overlay Wear Plate, Chrome Carbide Fusion Plate
- A. Schulman LP642 Narrow Molecular Weight Copolymer, High-Density Polyethylene
- ExxonMobil 625 Mobil SHC 600 Series
Copyright © lookpolymers.com All Rights Reserved