Dow FLEXOMER™ DFDB-1088 NT Very Low Density Polyethylene (VLDPE) Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Dow Chemical
Trade Name FLEXOMER™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow FLEXOMER™ DFDB-1088 NT Very Low Density Polyethylene (VLDPE) Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FLEXOMER™ DFDB-1088 NT is an ethylene-butene copolymer produced via gas phase polymerization from Dow. It can be utilized in monolayer and co-extruded films and in blends with other polyolefins to enhance melt strength and toughness of the structure. Information provided by Dow
Physical Properties Metric English Comments
Density 0.884 g/cc
0.0319 lb/in³
ASTM D792
High Load Melt Index 4.0 g/10 min

@Load 21.6 kg,
Temperature 190 °C
4.0 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238
Melt Index of Compound 0.10 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.10 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 83
83
1 sec; molded and tested in accordance with ASTM D4976; ASTM D2240
83
83
5 sec; molded and tested in accordance with ASTM D4976; ASTM D2240
Tensile Strength at Break 4.83 MPa
700 psi
Molded and tested in accordance with ASTM D4976; ASTM D638
Elongation at Break 300 %
300 %
Molded and tested in accordance with ASTM D4976; ASTM D638
Flexural Modulus 0.0331 GPa
4.80 ksi
2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 A
Thermal Properties Metric English Comments
Melting Point 114 °C
237 °F
Dow Method (DSC)
Glass Transition Temp, Tg -48.9 °C
-56.0 °F
Dow Method