Dow DNDA-7147 NT 7 Linear Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer Dow Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow DNDA-7147 NT 7 Linear Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DOW DNDA-7147 NT 7 is produced using UNIPOL™ PE process technology. It is intended for use in injection molding applications such as food containers, housewares and lids. Information provided by Dow
Physical Properties Metric English Comments
Density 0.926 g/cc
0.0335 lb/in³
ASTM D792
ESCR 100% Igepal® 5.0 hour

@Temperature 50.0 °C
5.0 hour

@Temperature 122 °F
F<sub>50</sub>; Molded and tested in accordance with ASTM D4976; ASTM D1693
Melt Index of Compound 50 g/10 min

@Load 2.16 kg,
Temperature 190 °C
50 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 52
52
Molded and tested in accordance with ASTM D4976; ASTM D2240
Tensile Strength at Break 7.58 MPa
1100 psi
Molded and tested in accordance with ASTM D4976; ASTM D638
Tensile Strength, Yield 9.65 MPa
1400 psi
Molded and tested in accordance with ASTM D4976; ASTM D638
Elongation at Break 120 %
120 %
Molded and tested in accordance with ASTM D4976; ASTM D638
Elongation at Yield 3.0 %
3.0 %
Molded and tested in accordance with ASTM D4976; ASTM D638
Flexural Modulus 0.421 GPa
61.0 ksi
2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B
Tensile Impact Strength 189 kJ/m²
90.0 ft-lb/in²
Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S
Thermal Properties Metric English Comments
Melting Point 124 °C
255 °F
Dow Method (DSC)
Crystallization Temperature 109 °C
228 °F
Dow Method (DSC)
Deflection Temperature at 0.46 MPa (66 psi) 45.0 °C
113 °F
Molded and tested in accordance with ASTM D4976; ASTM D648
Vicat Softening Point 90.0 °C
194 °F
ASTM D1525
Brittleness Temperature <= -76.1 °C
<= -105 °F
Molded and tested in accordance with ASTM D4976; ASTM D746