Dow DMDA-8965 NT 7 High Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE
Manufacturer Dow Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow DMDA-8965 NT 7 High Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DOW DMDA-8965 NT 7 is produced using UNIPOL™ process technology. It is intended for use in thin wall injection molding applications such as food containers. Information provided by Dow
Physical Properties Metric English Comments
Density 0.952 g/cc
0.0344 lb/in³
ASTM D792
Melt Index of Compound 66 g/10 min

@Load 2.16 kg,
Temperature 190 °C
66 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 59
59
Molded and tested in accordance with ASTM D4976; ASTM D2240
Tensile Strength at Break 28.3 MPa
4100 psi
Molded and tested in accordance with ASTM D4976; ASTM D638
Tensile Strength, Yield 17.2 MPa
2500 psi
Molded and tested in accordance with ASTM D4976; ASTM D638
Elongation at Break 10 %
10 %
Molded and tested in accordance with ASTM D4976; ASTM D638
Elongation at Yield 1.0 %
1.0 %
Molded and tested in accordance with ASTM D4976; ASTM D638
Flexural Modulus 1.00 GPa
145 ksi
2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B
Tensile Impact Strength 63.0 kJ/m²
30.0 ft-lb/in²
Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S
Thermal Properties Metric English Comments
Melting Point 128 °C
262 °F
Dow Method (DSC)
Crystallization Temperature 116 °C
241 °F
Dow Method (DSC)
Deflection Temperature at 0.46 MPa (66 psi) 68.9 °C
156 °F
Molded and tested in accordance with ASTM D4976; ASTM D648
Vicat Softening Point 122 °C
252 °F
ASTM D1525
Brittleness Temperature -20.0 °C
-4.00 °F
Molded and tested in accordance with ASTM D4976; ASTM D746