- Diamond Polymers Softflex® 6538 Thermoplastic Elastomer Alloy, Clear
Diamond Polymers Softflex® 6538 Thermoplastic Elastomer Alloy, Clear
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | Softflex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers Softflex® 6538 Thermoplastic Elastomer Alloy, Clear.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm @Thickness 3.17 mm |
0.0040 - 0.0080 in/in @Thickness 0.125 in |
Direction of Flow; ASTM D955 |
| 0.0040 - 0.0080 cm/cm @Thickness 3.17 mm |
0.0040 - 0.0080 in/in @Thickness 0.125 in |
Transverse to Flow; ASTM D955 | |
| Melt Flow | 3.8 g/10 min @Load 2.16 kg, Temperature 175 °C |
3.8 g/10 min @Load 4.76 lb, Temperature 347 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55 - 65 | 55 - 65 | ASTM D2240 |
| Tensile Strength at Break | 57.2 MPa | 8300 psi | chs 20 in/min; ASTM D412 |
| Tensile Strength, Yield | 15.2 MPa | 2200 psi | chs 20 in/min; 50% elongation; ASTM D412 |
| 20.7 MPa | 3000 psi | chs 20 in/min; 100% elongation; ASTM D412 | |
| 41.3 MPa | 5990 psi | chs 20 in/min; 300% elongation; ASTM D412 | |
| Elongation at Break | 360 % | 360 % | chs 20 in/min; ASTM D412 |
| Flexural Modulus | 0.2549 GPa | 36.97 ksi | chs 0.05 in/min; ASTM D790 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |
Users viewing this material also viewed the following:
- NCMT NanoPAC™ S202 High Performance Polypropylene Nanocomposite
- SABIC Innovative Plastics Cycoloy® C1200 PC+ABS
- DSM Akulon® K-FHG12 (Dry) 60% Glass Reinforced Nylon 6 (North America) (discontinued **)
- Multibase Multi-Flamâ„¢ 2012 HFR 24 Polypropylene
- Solvay Specialty Polymers Ixef® 1022 Polyarylamide (PARA), 50% Glass Fiber (Conditioned)
- Solvay Specialty Polymers Veradel® 3300 PREM Polyethersulfone (PESU)
- Arkema Group VOLTALEF® 302 PCTFE
- Weartech International WT-190 Cobalt Hardfacing & Wear Resistant Alloy
Copyright © lookpolymers.com All Rights Reserved