Lubrizol Advanced Materials PEARLTHANE® D11H92S Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Lubrizol Advanced Materials Manufacturing S. S.L. (Former Merquinsa) |
| Trade Name | Pearlthane® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Advanced Materials PEARLTHANE® D11H92S Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PEARLTHANE® D11H92S is a high performance polycaprolactone copolyester based TPU, supplied in form of translucent, colorless pellets, featuring excellent flow and mechanical properties and an outstanding low compression set value and high temperature resistance. Product recommended for injection-molding applications with an extremely short cycle time.All information provided by Merquinsa
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min @Load 21.6 kg, Temperature 201 - 211 °C |
10 g/10 min @Load 47.6 lb, Temperature 394 - 412 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 92 | 92 | ASTM D2240 |
| Tensile Strength, Yield | 46.00 MPa | 6672 psi | ASTM D412 |
| Elongation at Break | 460 % | 460 % | ASTM D412 |
| 100% Modulus | 0.009997 GPa | 1.450 ksi | ASTM D412 |
| 300% Modulus | 0.02100 GPa | 3.046 ksi | ASTM D412 |
| Tear Strength | 156 kN/m | 890 pli | ASTM D624 (Die C) |
| Abrasion | 20 | 20 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 13 % @Temperature 23.0 °C, Time 252000 sec |
13 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395B |
| 19 % @Temperature 70.0 °C, Time 79200 sec |
19 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395B | |
| 36 % @Temperature 100 °C, Time 252000 sec |
36 % @Temperature 212 °F, Time 70.0 hour |
ASTM D395B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 201 - 211 °C | 394 - 412 °F | MQSA 111 |
| Glass Transition Temp, Tg | -43.0 °C | -45.4 °F | DSC, 10°C/min; ISO 11357-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 190 °C | 374 °F | |
| Nozzle Temperature | 200 °C | 392 °F | |
| Zone 1 | 195 °C | 383 °F | Compression Zone |
| Zone 2 | 195 °C | 383 °F | Metering Zone |
| Mold Temperature | 35.0 °C | 95.0 °F | |
| Moisture Content | <= 0.10 % | <= 0.10 % | MQSA 44 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 5 T 20 FRG 2 PA6, 5% glass fibre, 20% mineral filling
- Polykemi AB POLYfill PPC T3020 Polypropylene Copolymer, Mineral Reinforced
- Ferro IP 780 Passivation Glasses (Pb-B-Si-Al; Pb-Si-Al; Si-Pb-Al Silicates)
- LG Chemical TR300 MABS, Flame Retardant, Transparency
- Taiwan Sheen Soon Sheenthane® D7620 Thermoplastic Polyurethane Elastomer
- Techmer ES HiFill® POM CO GF/M30 UV BK 30% Glass Milled/Glass Fiber Filled
- Techmer ES Plaslube® J-1/CF/15/TF/20 NAT PA66
- Teknor Apex Sinvicomp SFE 7000 Polyvinyl Chloride, Flexible
- Loctite® 392 Rapid Fixture Structural Adhesive
Copyright © lookpolymers.com All Rights Reserved