Diamond Polymers DIAMALOY VP22 NATURAL 1001B Blow Molding Grade, Flame Retardant ABS

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer Diamond and Network Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Diamond Polymers DIAMALOY VP22 NATURAL 1001B Blow Molding Grade, Flame Retardant ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.24 g/cc
1.24 g/cc
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Melt Flow 0.30 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 0.30 g/10 min

@Load 11.0 lb,
Temperature 392 °F
 ASTM D1238
1.5 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 1.5 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 98
98
ASTM D785
Tensile Strength, Yield 35.8 MPa
5190 psi
chs 2.0 in/min; ASTM D638
Flexural Modulus 1.929 GPa
279.8 ksi
chs 0.05 in/min; ASTM D790
Izod Impact, Notched 2.14 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
 4.01 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Vicat Softening Point 102 °C

@Load 1.00 kg,
Thickness 3.17 mm
 216 °F

@Load 2.20 lb,
Thickness 0.125 in
 ASTM D1527
Flammability, UL94 V-0

@Thickness 1.59 mm
 V-0

@Thickness 0.0625 in
5VA

@Thickness 3.17 mm
 5VA

@Thickness 0.125 in