Diamond Polymers Centrex® 833 Sheet Extrusion Grade

Category Polymer , Thermoplastic , ASA Polymer
Manufacturer Diamond and Network Polymers
Trade Name Centrex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Diamond Polymers Centrex® 833 Sheet Extrusion Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Centrex 833 resin is a high-gloss, high-impact grade of ASA (acrylonitrile-styrene-acrylate) with good resistance to weather aging. It has good melt strength for extrusion and thermoforming, and it can be easily coextruded. The recommended substrate is ABS (acrylonitrile-butadiene-styrene) resin.Applications: Typical applications for Centrex 833 resin includes exterior parts requiring high gloss, such as spas; marine components, boat hulls and decks; doors, covers, and trim for recreational vehicles; swimming pool steps; and fiberglass-reinforced plastic replacements. As with any product, use of Centrex 833 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Melt Flow 8.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
8.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 89
89
ASTM D785
Tensile Strength, Yield 31.7 MPa
4600 psi
chs 2.0 in/min; ASTM D638
Tensile Modulus 1.60 GPa
232 ksi
chs 2.0 in/min; ASTM D638
Flexural Strength 51.7 MPa
7500 psi
chs 0.05 in/min; ASTM D790
Flexural Modulus 16.0 GPa
2320 ksi
tangent; chs 0.05 in/min; ASTM D790
Izod Impact, Notched 1.17 J/cm

@Thickness 3.17 mm,
Temperature -30.0 °C
2.19 ft-lb/in

@Thickness 0.125 in,
Temperature -22.0 °F
ASTM D256
1.33 J/cm

@Thickness 3.17 mm,
Temperature -18.0 °C
2.49 ft-lb/in

@Thickness 0.125 in,
Temperature -0.400 °F
ASTM D256
3.47 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
6.50 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
ASTM D256
Impact Test 30.0 J

@Temperature -30.0 °C
22.1 ft-lb

@Temperature -22.0 °F
ASTM D3763
38.0 J

@Temperature -18.0 °C
28.0 ft-lb

@Temperature -0.400 °F
ASTM D3763
43.0 J

@Temperature 23.0 °C
31.7 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear 100 µm/m-°C
55.6 µin/in-°F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 77.0 °C
171 °F
0.125";; ASTM D648
Flammability, UL94 HB
HB
Optical Properties Metric English Comments
Gloss 75 - 85 %
75 - 85 %
Formed; 60°; ASTM D523
90 - 100 %
90 - 100 %
Sheet; 60°; ASTM D523