Diamond Polymers ASA 5946

Category Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
Manufacturer Diamond and Network Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Diamond Polymers ASA 5946.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: ASA Weatherable Polymer, Injection Molding Grade, Very High HeatInformation provided by Diamond Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D955
Melt Flow 0.20 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 0.20 g/10 min

@Load 11.0 lb,
Temperature 392 °F
 Procedure A; ASTM D1238
1.3 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 1.3 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 Procedure A Condition I; ASTM D1238
4.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 4.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 Procedure A; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 104
104
ASTM D785
Tensile Strength, Yield 51.7 MPa
7500 psi
chs 2 in/min; ASTM D638
Flexural Modulus 2.69 GPa
390 ksi
Tangent, chs 0.05 in/min; ASTM D790
Izod Impact, Notched 1.07 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
 2.00 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
 bar; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 100 °C
212 °F
0.125 in bar Unannealed/Conditioned 40 hours at 23°C; ASTM D648
110 °C
230 °F
0.25 in bar Unannealed/Conditioned 40 hours at 23°C; ASTM D648
Vicat Softening Point 130 °C
266 °F
0.125 inch, 1 Kg; ASTM D1525