Diamond Polymers ABS 3501 Black 1302 Injection Molding Grade

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Diamond and Network Polymers
Trade Name
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Diamond Polymers ABS 3501 Black 1302 Injection Molding Grade.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Melt Flow 1.1 g/10 min
<br>@Load 5.00 kg,<br> Temperature 200 °C
 1.1 g/10 min
<br>@Load 11.0 lb,<br> Temperature 392 °F
 ASTM D1238
4.3 g/10 min
<br>@Load 3.80 kg,<br> Temperature 230 °C
 4.3 g/10 min
<br>@Load 8.38 lb,<br> Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 106
106
ASTM D785
Tensile Strength, Yield 42.7 MPa
6190 psi
chs 2 in/min; ASTM D638
Flexural Modulus 2.384 GPa
345.8 ksi
tangent; chs 0.05 in/min; ASTM D790
Izod Impact, Notched 3.47 J/cm
<br>@Thickness 3.17 mm,<br> Temperature 23.0 °C
 6.50 ft-lb/in
<br>@Thickness 0.125 in,<br> Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Vicat Softening Point 104 °C
<br>@Load 1.00 kg,<br> Thickness 3.17 mm
 219 °F
<br>@Load 2.20 lb,<br> Thickness 0.125 in
 ASTM D1525
Flammability, UL94 HB
<br>@Thickness 1.59 mm
 HB
<br>@Thickness 0.0625 in
HB
<br>@Thickness 3.17 mm
 HB
<br>@Thickness 0.125 in