- Daikin DAI-EL LT-302 Fluoroelastomer, Low Temperature Grade, 64% Fluorine Content
Daikin DAI-EL LT-302 Fluoroelastomer, Low Temperature Grade, 64% Fluorine Content
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Daikin Industries |
| Trade Name | DAI-EL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Daikin DAI-EL LT-302 Fluoroelastomer, Low Temperature Grade, 64% Fluorine Content.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Flexible up to -30°C, excellent low temperature sealing.Information provided by Daikin Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.80 g/cc | 1.80 g/cc | at 25°C |
| Mooney Viscosity | 30 @Temperature 121 °C |
30 @Temperature 250 °F |
ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 65 | 65 | Peak value, at 25°C |
| Tensile Strength at Break | 18.1 MPa | 2630 psi | |
| Tensile Strength, Yield | 3.50 MPa @Strain 100 % |
508 psi @Strain 100 % |
|
| Elongation at Break | 250 % | 250 % | |
| Tear Strength | 24.0 kN/m | 137 pli | at 25°C |
| Compression Set | 8.0 % | 8.0 % | 70 hours at 25°C |
| 9.0 % @Temperature 100 °C |
9.0 % @Temperature 212 °F |
70 hours | |
| 12 % @Temperature 175 °C |
12 % @Temperature 347 °F |
70 hours | |
| 17 % @Temperature 200 °C |
17 % @Temperature 392 °F |
70 hours |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Minimum Service Temperature, Air | -31.0 °C | -23.8 °F | TR test, TR10 |
| -29.5 °C | -21.1 °F | Gehman torsion test, T10 | |
| -25.0 °C | -13.0 °F | Gehman torsion test, T2 | |
| -22.0 °C | -7.60 °F | TR test, TR70 | |
| Brittleness Temperature | -38.0 °C | -36.4 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 160 °C | 320 °F | Cure Measuring Temperature |
| Cure Time | 1.50 min | 0.0250 hour | Curelastmeter |
Users viewing this material also viewed the following:
- Pau Tai UNISTAB BT-11 Organo Tin Stabilizer
- LG Chemical LUMID GP2430B(W) PA66+GF43%, General Purpose
- SABIC Innovative Plastics ULTEM 1010 PEI
- Spartech Polypedic Modified Low Density Polyethylene
- Polyram PlusTek RB145 Nylon 6, General Purpose
- ChevronTexaco Clarity® ISO 100 Saw Guide Oil
- Radici Raditer® B RVA 200 Polybutylene Terephthalate with 20% Glass fiber
- Polymer Resources PPX-MF-FR3 Modified PPO, UL 94 V-0 with HDT of 230 F, Mineral Reinforced (Unverified Da
- LTL Color Compounds ColorFast® NY1GF330 Nylon 6, 33% Glass-Filled
Copyright © lookpolymers.com All Rights Reserved