Daikin DAI-EL G-801 Fluoroelastomer Copolymer, Peroxide Curable Grade, 66% Fluorine Content

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer Daikin Industries
Trade Name DAI-EL
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Daikin DAI-EL G-801 Fluoroelastomer Copolymer, Peroxide Curable Grade, 66% Fluorine Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Offers excellent chemical and steam resistance. Offers good mechanical characteristics.Features: Good low-temperature and elasticity characteristics.Information provided by Daikin Industries.
Physical Properties Metric English Comments
Specific Gravity 1.80 g/cc
1.80 g/cc
at 25°C
Mooney Viscosity 37

@Temperature 121 °C
37

@Temperature 250 °F
ML 1+10
Mechanical Properties Metric English Comments
Hardness, Shore A 66
66
Peak value, at 25°C
Tensile Strength at Break 22.0 MPa
3190 psi
Tensile Strength, Yield 2.00 MPa

@Strain 100 %
290 psi

@Strain 100 %
Elongation at Break 450 %
450 %
Tear Strength 20.6 kN/m
118 pli
at 25°C
Taber Abrasion, mg/1000 Cycles 155
155
H-22 abrasive wheel, load: 1000g x 2
Compression Set 21 %
21 %
70 hours at 25°C
17 %

@Temperature 100 °C
17 %

@Temperature 212 °F
70 hours
25 %

@Temperature 175 °C
25 %

@Temperature 347 °F
70 hours
38 %

@Temperature 200 °C
38 %

@Temperature 392 °F
70 hours
Thermal Properties Metric English Comments
Minimum Service Temperature, Air -19.0 °C
-2.20 °F
TR test, TR10
-15.5 °C
4.10 °F
Gehman torsion test, T10
-10.0 °C
14.0 °F
TR test, TR70
-10.0 °C
14.0 °F
Gehman torsion test, T2
Brittleness Temperature -25.0 °C
-13.0 °F
Processing Properties Metric English Comments
Processing Temperature 160 °C
320 °F
Cure Measuring Temperature
Cure Time 2.50 min
0.0417 hour
Curelastmeter