Daelim H&L Plavis G40 Aromatic Polyimide, 40% Graphite Filled, Machined Parts
| Category | Polymer , Thermoset , Polyimide, TS |
| Manufacturer | Daelim H&L Super Engineering Plastics |
| Trade Name | Plavis |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Daelim H&L Plavis G40 Aromatic Polyimide, 40% Graphite Filled, Machined Parts.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Higher abrasion resistance than G15, high value stability and very low friction coefficient propertyInformation provided by Daelim H&L
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.85 % | 0.85 % | 50% RH; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 68 - 78 | 68 - 78 | ASTM D785 |
| Tensile Strength, Ultimate | 41.1 MPa @Temperature 260 °C |
5960 psi @Temperature 500 °F |
ASTM D1708 |
| 73.2 MPa @Temperature 23.0 °C |
10600 psi @Temperature 73.4 °F |
ASTM D1708 | |
| Tensile Strength, Yield | 32.6 MPa @Strain 1.00 % |
4720 psi @Strain 1.00 % |
ASTM D95 |
| 115 MPa @Strain 10.0 % |
16600 psi @Strain 10.0 % |
ASTM D95 | |
| Elongation at Break | 5.7 % @Temperature 260 °C |
5.7 % @Temperature 500 °F |
ASTM D1708 |
| 6.5 % @Temperature 23.0 °C |
6.5 % @Temperature 73.4 °F |
ASTM D1708 | |
| Flexural Strength | 48.1 MPa @Temperature 260 °C |
6980 psi @Temperature 500 °F |
ASTM D790 |
| 90.4 MPa @Temperature 23.0 °C |
13100 psi @Temperature 73.4 °F |
ASTM D790 | |
| Flexural Modulus | 2.76 GPa @Temperature 260 °C |
400 ksi @Temperature 500 °F |
ASTM D790 |
| 4.848 GPa @Temperature 23.0 °C |
703.2 ksi @Temperature 73.4 °F |
ASTM D790 | |
| Compressive Modulus | 3.3864 GPa @Temperature 23.0 °C |
491.16 ksi @Temperature 73.4 °F |
ASTM D695 |
| Izod Impact, Notched (ISO) | 4.3164 kJ/m² | 2.0543 ft-lb/in² | ASTM D256 |
| Coefficient of Friction | 0.14 | 0.14 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 3.40 µm/m-°C @Temperature 23.0 - 260 °C |
1.89 µin/in-°F @Temperature 73.4 - 500 °F |
ASTM D696 |
| Decomposition Temperature | 616 °C | 1140 °F | |
| Oxygen Index | 53.7 % | 53.7 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10000 ohm-cm - 1e+05 @Temperature 23.0 °C |
10000 ohm-cm - 1e+05 @Temperature 73.4 °F |
ASTM D257 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| 50% Weight Reduction Time (Minutes) | 240 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8612 (849) (UF) Synthetic Oil
- KYDEX® 6565(d) Decorative Low Heat Release Thermoplastic Sheet, Aviation
- Henkel Turco EA Stripper R 6955 GL Paint Remover
- SABIC Innovative Plastics NORYL SE100X PPE+PS (Asia Pacific)
- Teknor Apex Telcar® TL 83-F943D22-NT Thermoplastic Elastomer
- A. Schulman POLYBATCH™ Tan LL60139/2 Concentrate Based In LLDPE
- Unipetrol C9 Fraction Redistillated
- Dow Corning 7096 CLEAR SEALANT
- Cyclewood Solutions Xylomer™ XM1-LA Injection Molding Compostable Resin
- Bhansali Engineering Abstron SE-32 ABS Sheet Extrusion Grade
Copyright © lookpolymers.com All Rights Reserved