- Daelim H&L Plavis G15 Aromatic Polyimide, 15% Graphite Filled, Direct Formed (Unverified Data**)
Daelim H&L Plavis G15 Aromatic Polyimide, 15% Graphite Filled, Direct Formed (Unverified Data**)
| Category | Polymer , Thermoset , Polyimide, TS |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Daelim H&L Plavis G15 Aromatic Polyimide, 15% Graphite Filled, Direct Formed
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Daelim H&L
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 68 - 78 | 68 - 78 | ASTM D785 |
| Tensile Strength, Ultimate | 38.6 MPa @Temperature 260 °C |
5600 psi @Temperature 500 °F |
ASTM D1708 |
| 72.5 MPa @Temperature 23.0 °C |
10500 psi @Temperature 73.4 °F |
ASTM D1708 | |
| Tensile Strength, Yield | 23.3 MPa @Strain 1.00 % |
3390 psi @Strain 1.00 % |
ASTM D95 |
| 106.0 MPa @Strain 10.0 % |
15380 psi @Strain 10.0 % |
ASTM D95 | |
| Elongation at Break | 5.4 % @Temperature 260 °C |
5.4 % @Temperature 500 °F |
ASTM D1708 |
| 8.7 % @Temperature 23.0 °C |
8.7 % @Temperature 73.4 °F |
ASTM D1708 | |
| Flexural Strength | 54.0 MPa @Temperature 260 °C |
7830 psi @Temperature 500 °F |
ASTM D790 |
| 86.2 MPa @Temperature 23.0 °C |
12500 psi @Temperature 73.4 °F |
ASTM D790 | |
| Flexural Modulus | 1.819 GPa @Temperature 260 °C |
263.8 ksi @Temperature 500 °F |
ASTM D790 |
| 3.1761 GPa @Temperature 23.0 °C |
460.65 ksi @Temperature 73.4 °F |
ASTM D790 | |
| Compressive Modulus | 2.3838 GPa @Temperature 23.0 °C |
345.74 ksi @Temperature 73.4 °F |
ASTM D695 |
| Shear Strength | 78.48 MPa @Temperature 23.0 °C |
11380 psi @Temperature 73.4 °F |
ASTM D732 |
| Izod Impact, Notched (ISO) | 4.5126 kJ/m² | 2.1477 ft-lb/in² | ASTM D256 |
| Coefficient of Friction | 0.20 | 0.20 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 3.50 µm/m-°C @Temperature 23.0 - 260 °C |
1.94 µin/in-°F @Temperature 73.4 - 500 °F |
ASTM D696 |
| Decomposition Temperature | 616 °C | 1140 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| 50% Weight Reduction Time (Minutes) | 240 |
Users viewing this material also viewed the following:
- Radici Radilon® CST 38FL (cond.) Nylon 6/66
- Lanxess Durethan® BKV 30 H2.0 EF 901510 Nylon 6, 30% Glass Fiber
- MetalTek MTEK 30-20 Cast UNS N08604 Heat Resistant Stainless Steel
- Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Conditioned)
- SCG Chemicals EL-Leneâ„¢ L2009F Linear Low Density Polyethylene Film
- Unitika CX-2500 PA6, Conditioned
- Zyvex Performance Materials Arovex™ HT 250 Nano-Engineered Composite Prepreg System
- Trelleborg Hypalon® H511 Chlorosulphonated Polyethylene
- Azoty Tarnow™ TARNOFORM 300 TF4 POM
- Axiall 11600 Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved