DSM Arnite® TZ6 280 BLK (NCP-4718/B) PBT-(GF+GB)40
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Bead Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Arnite® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Arnite® TZ6 280 BLK (NCP-4718/B) PBT-(GF+GB)40.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Glass Reinforced, 20% Glass Beads Reinforced
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 |
| Water Absorption | 0.25 % | 0.25 % | Sim. To ISO 62 |
| Moisture Absorption | 0.150 % | 0.150 % | Sim. To ISO 62 |
| Viscosity | 20000 cP @Shear Rate 100000 1/s, Temperature 230 °C |
20000 cP @Shear Rate 100000 1/s, Temperature 446 °F |
|
| 20000 cP @Shear Rate 100000 1/s, Temperature 250 °C |
20000 cP @Shear Rate 100000 1/s, Temperature 482 °F |
||
| 20000 cP @Shear Rate 100000 1/s, Temperature 270 °C |
20000 cP @Shear Rate 100000 1/s, Temperature 518 °F |
||
| 300000 cP @Shear Rate 1.00 1/s, Temperature 270 °C |
300000 cP @Shear Rate 1.00 1/s, Temperature 518 °F |
||
| 500000 cP @Shear Rate 1.00 1/s, Temperature 250 °C |
500000 cP @Shear Rate 1.00 1/s, Temperature 482 °F |
||
| 700000 cP @Shear Rate 1.00 1/s, Temperature 230 °C |
700000 cP @Shear Rate 1.00 1/s, Temperature 446 °F |
||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 100 MPa | 14500 psi | ISO 527-1/-2 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-1/-2 |
| Tensile Modulus | 9.10 GPa | 1320 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 3.49 J/cm² @Temperature 23.0 °C |
16.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.550 J/cm² @Temperature -30.0 °C |
2.62 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.699 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.1 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable EAC31L Polyvinyl Chloride, Flexible (PVC, Flexible)
- MV Labs PT485 [Pt(NH3)4][PtCl4] Tetramineplatinum(II) tetrachloroplatinate(II)
- Karina E 898-10/161-IS-RG White PVC Compound
- Kazanorgsintez 108-273 Thermostabilized Low Density Polyethylene Composition for Radiation Modification
- Saint-Gobain Rulon® 1337 Bearing/Seal PTFE
- Shinkong Synthetic Fibers Shinite® PP4220 PP, High Impact, Fire Retardant
- Sibur BSK-1500 Styrene-Butadiene Rubber (SBR)
- Trelleborg Emerson & Cuming Eccobond® 15 Variable Hardness Catalyst
- Dow Corning SLYGARD® 537 ONE PART DIELECTRIC GEL
- Chosun Refractories joint-1 Blast Furnace Runner Refractory
Copyright © lookpolymers.com All Rights Reserved