Cossa Polimeri ESTABLEND 4500 Polycarbonate ABS Blend
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTABLEND |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTABLEND 4500 Polycarbonate ABS Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate and Acrylonitrile Butadiene Styrene blendGood impact resistance at low temperature, high glossInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D 955 |
| Melt Flow | 20 g/10 min @Load 5.00 kg, Temperature 260 °C |
20 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 42.0 MPa | 6090 psi | ASTM D 638 |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | ASTM D 638 |
| Elongation at Break | 40 % | 40 % | ASTM D 638 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D 790 |
| Izod Impact, Notched | 4.20 J/cm @Temperature 0.000 °C |
7.87 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 |
| 4.80 J/cm @Temperature 23.0 °C |
8.99 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 113 °C @Load 5.00 kg |
235 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| 125 °C @Load 0.999 kg |
257 °F @Load 2.20 lb |
50°C/hr; ASTM D 1525 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 750 °C @Thickness 2.00 mm |
1380 °F @Thickness 0.0787 in |
I.E.C. 695-2-1 |
Users viewing this material also viewed the following:
- Karina E 27/8-GIN Fume MBATCH (SP31452) for PVC
- LATI Kelon® B FR H CETG/250-V0 PA 6, Glass/Mineral Reinforced, Flame Retardant, Heat Stabilized
- Techmer ES Plaslube® J-4/30/TF/13/SI/2 BK223 PA6/12
- Dow Corning JCR 6101 UP
- Daelim H&L Plavis-G15 DF 15% Graphite Filled Aromatic Polyimide Bearing
- Aaron Industries AAROPRENE® AEN 6600-1 Nylon 6/6 Engineered Resin
- Arkema Group Evatane® 1350 VN 5 Ethylene Vinyl Acetate
- Dynasol Solprene® 233 Medium CIS Polybutadiene
- Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 16% Plasticizer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved