Cosmic Plastics 6220F Short Glass Fiber Filled Iso Diallyl Phthalate Molding Compound
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled , Filled/Reinforced Thermoset |
| Manufacturer | Cosmic Plastics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cosmic Plastics 6220F Short Glass Fiber Filled Iso Diallyl Phthalate Molding Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.79 g/cc | 0.0647 lb/in³ | |
| Apparent Bulk Density | 0.720 g/cc | 0.0260 lb/in³ | |
| Water Absorption | 0.25 % | 0.25 % | 48 hrs, 50°C |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | typical. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
| Flexural Strength | 97.0 MPa | 14100 psi | |
| Compressive Strength | 172 MPa | 24900 psi | |
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.0 µm/m-°C @Temperature 20.0 °C |
13.9 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Heat Distortion temperature |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | |
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | |
| Dielectric Constant | 4.1 @Frequency 1000 Hz |
4.1 @Frequency 1000 Hz |
Wet |
| 4.1 @Frequency 1e+6 Hz |
4.1 @Frequency 1e+6 Hz |
Wet | |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | Wet, Step by Step |
| Dissipation Factor | 0.0090 @Frequency 1000 Hz |
0.0090 @Frequency 1000 Hz |
Wet |
| 0.013 @Frequency 1e+6 Hz |
0.013 @Frequency 1e+6 Hz |
Wet | |
| Arc Resistance | 155 sec | 155 sec |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 165 °C | 275 - 329 °F | Molding temperature |
Users viewing this material also viewed the following:
- Polymer Resources TPSF-FRG30 Polybutylene Terephthalate, Structural Foam, 30% Glass Reinforced, Flame Retardant
- Rogers Corporation RO3035 Ceramic-Filled PTFE Composite, High Frequency Circuit Material
- Nilit RECONYL B F Recycled nylon 6 for injection molding
- LATI LATAN 13 G/15 15% Glass Fiber Reinforced Polyoxymethylene Copolymer (POM) (discontinued **)
- Momentive Performance Materials HCJ-48 Boron Nitride (BN) Powder
- LATI Larpeek 50 K/30 PEEK, 30% Carbon Fiber Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66
- Techmer ES Electrafil® J-3/CF/10 Nylon 6, 10% Carbon Fiber Reinforced
- Silberline Sparkle Silvet® 760-20-J
- SABIC Innovative Plastics Lexan® HPH4504H PPC
Copyright © lookpolymers.com All Rights Reserved